A kind of phosphogypsum wall brick and preparation method thereof
A technology of gypsum wall and phosphogypsum, which is applied in the field of phosphogypsum wall bricks and its preparation, can solve the problems that harmful impurities cannot be removed, phosphogypsum raw materials are not pretreated, and the performance of products is affected, so as to realize the comprehensive utilization of building materials resources , Improve the compactness and softening coefficient, and eliminate the effect of adverse effects
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0021] Example 1
[0022] The phosphogypsum wall brick provided in this embodiment is made of the following parts by weight of raw materials: 100 parts of phosphogypsum, 10 parts of calcium carbide slag, 12 parts of hydraulic admixture, 5 parts of coarse stone, 10 parts of stone powder, Yuan Ming 1.5 parts of powder, 3 parts of water glass, 0.2 parts of calcium formate, 4 parts of calcium lignosulfonate. Among them, phosphogypsum is granular and can be used as inert aggregate in the product.
[0023] The preparation method of the phosphogypsum wall brick is: mixing phosphogypsum and calcium carbide slag, and spraying with water mist; granulating the mixture of phosphogypsum and calcium carbide slag to obtain spherical particles with a particle size of 8 -15mm, and air-dried under natural conditions; mix spherical particles with hydraulic admixtures, aggregates and additives, add water and stir to form a uniform slurry; inject the slurry into the molding machine for compression mo...
Example Embodiment
[0025] Example 2
[0026] The phosphogypsum wall brick provided in this embodiment is made of the following raw materials in parts by weight: 100 parts of phosphogypsum, 6 parts of calcium carbide slag, 15 parts of hydraulic admixture, 8 parts of coarse stone, 16 parts of stone powder, Yuan Ming 2 parts of powder, 4 parts of water glass, 0.1 part of calcium formate, 2 parts of calcium lignosulfonate.
[0027] The preparation method of the phosphogypsum wall brick is: mixing phosphogypsum and calcium carbide slag, and spraying with water mist; granulating the mixture of phosphogypsum and calcium carbide slag to obtain cubic particles with a particle size of 9 -20mm, and air-dried under natural conditions; mix the spherical particles with hydraulic admixtures, aggregates and additives, add water and stir to form a uniform slurry; inject the slurry into the molding machine for compression molding, the molding pressure is 20MPa; The molded products are naturally cured to obtain phosp...
Example Embodiment
[0029] Example 3
[0030] The phosphogypsum wall brick provided in this embodiment is made of the following raw materials by weight: 100 parts of phosphogypsum, 8 parts of calcium carbide slag, 8 parts of hydraulic admixture, 7.5 parts of coarse stone, 15 parts of stone powder, Yuan Ming 0.5 parts of powder, 5 parts of water glass, 0.05 parts of calcium formate, 6 parts of calcium lignosulfonate.
[0031] The preparation method of the phosphogypsum wall brick is: mixing phosphogypsum and calcium carbide slag, and spraying with water mist; granulating the mixture of phosphogypsum and calcium carbide slag to obtain tetrahedral particles with a particle size of 9- 20mm, and air-dried under natural conditions; mix spherical particles with hydraulic admixtures, aggregates and additives, add water and stir to form a uniform slurry; inject the slurry into the molding machine for compression molding, the molding pressure is 8MPa; The molded product is naturally cured to produce phosphogy...
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap