Protection method for removing corrosion on surface of aluminum alloy

A technology for aluminum alloy surface and corrosion protection, which is applied to the device for coating liquid on the surface, metal material coating process, coating and other directions, which can solve the problems of secondary corrosion, difficult to completely remove the rust layer, and high labor intensity. Effectively remove and eliminate adverse effects

Inactive Publication Date: 2019-09-24
AVIC BEIJING INST OF AERONAUTICAL MATERIALS
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The methods of manual derusting, chemical solution derusting and mechanical shot blasting (sand) derusting, which are usually used to remove corrosion on the surface of aluminum alloys, have poor derusting quality, difficult to completely remove deep rust layers, high labor intensity, and easy to cause corrosion. Secondary corrosion and other shortcomings, and currently lack of convenient, fast and effective means of protection

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Provided is a method for corrosion protection on an aluminum alloy surface, comprising the following steps:

[0025] Step 1. Removal of floating rust on the corroded parts of the aluminum alloy surface

[0026] Mechanically polish the corroded parts of the aluminum alloy surface until the surface reveals a metallic luster, and use an organic solvent to clean the polished surface;

[0027] Step 2. Removal of deep corrosion products on the aluminum alloy surface

[0028] Apply aluminum alloy anti-corrosion product paste to the surface of aluminum alloy after mechanical polishing, and keep it for 0.5h~2h after application; when the anti-corrosion product paste is dry, clean the coated area to remove the attachment on the aluminum alloy surface;

[0029] Step 3, aluminum alloy surface oxidation

[0030] Apply an aluminum alloy surface oxide paste to the aluminum alloy surface coated with aluminum alloy corrosion product paste, and keep the oxide paste for 0.5h to 2h after...

Embodiment 2

[0037] Provided is a method for corrosion protection on an aluminum alloy surface, comprising the following steps:

[0038] Step 1. Removal of floating rust on the corroded parts of the aluminum alloy surface

[0039] Mechanically polish the corroded parts of the aluminum alloy surface until the surface reveals a metallic luster, and use an organic solvent to clean the polished surface;

[0040] Step 2. Removal of deep corrosion products on the aluminum alloy surface

[0041] Apply aluminum alloy anti-corrosion product paste to the surface of aluminum alloy after mechanical polishing, and keep it for 0.5h~2h after application; when the anti-corrosion product paste is dry, clean the coated area to remove the attachment on the aluminum alloy surface;

[0042] Step 3, aluminum alloy surface oxidation

[0043] Apply an aluminum alloy surface oxide paste to the aluminum alloy surface coated with aluminum alloy corrosion product paste, and keep the oxide paste for 0.5h to 2h after...

Embodiment 3

[0050] Including the following steps:

[0051] Step 1. Removal of floating rust on the corroded parts of the aluminum alloy surface

[0052] Use tools such as sandpaper, bristle brushes or grinding wheels to mechanically polish the corroded parts of the aluminum alloy surface until the surface reveals a metallic luster, and use cotton yarn or cotton cloth dipped in organic solvents such as gasoline, acetone or solvent-based cleaning agents to polish the polished surface After cleaning, dry the treated surface naturally in the air or dry it with clean compressed air;

[0053] Step 2. Removal of deep corrosion products on the aluminum alloy surface

[0054] Stir the aluminum alloy anti-corrosion product paste to a uniform paste, apply it to the mechanically polished aluminum alloy surface with a brush or scraper, and keep it for 0.5h~2h after coating; when the anti-corrosion product paste is dry, use a brush, cotton cloth or a scraper to remove the residual de-corrosion produc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a protection method for removing corrosion on the surface of an aluminum alloy. The protection method comprises a removal step of floating rust on corroded parts on the surface of the aluminum alloy, the removal step deep corrosion products on the surface of the aluminum alloy, an oxidation step on the surface of the aluminum alloy, and a protection step on the surface of the aluminum alloy after corrosion removing. According to the protection method, the corrosion products on the surface of the aluminum alloy are removed by adopting an aluminum alloy de-corrosion product paste, not only the corrosion products on the surface of the aluminum alloy can be quickly and effectively removed, but also the adverse effect of a chemical reagent on uncorroded parts on the surface of the aluminum alloy in the rust removing process is also eliminated; then the surface of the aluminum alloy is oxidized by adopting an aluminum alloy surface oxidation paste, so that a protective film with good binding force to an organic film layer and with a certain corrosion resistance is generated; and finally, the final purpose of protection is achieved by coating a corrosion inhibitor, an organic coating or the like.

Description

technical field [0001] The invention relates to the technical field of corrosion removal of aluminum alloy materials, in particular to a corrosion protection method for aluminum alloy surfaces. Background technique [0002] Aluminum alloy materials have a series of outstanding advantages such as high strength, low specific gravity and good formability, and have been widely used in aerospace, construction, mechanical automation and other fields. However, during use, with the failure of the anodized surface or surface protective coating, the aluminum alloy surface is extremely vulnerable to corrosion from the atmospheric environment, which causes serious safety hazards in the equipment. Therefore, it is necessary to remove the corrosion products on the surface of the aluminum alloy in a timely manner and protect the cleaned parts to ensure the safety and service life of the equipment. [0003] The methods of manual derusting, chemical solution derusting and mechanical shot bl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C23G1/12C23C22/05C23F11/00B05D7/14
CPCB05D7/14C23C22/05C23F11/00C23G1/125
Inventor 姜国杰刘明辉宇波孙志华
Owner AVIC BEIJING INST OF AERONAUTICAL MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com