Injectable breast repair material, its preparation method and its application
A repair material and breast technology, which is applied in the fields of breast repair materials, plastic surgery and plastic surgery materials, can solve the problems of low fat survival rate, fat cell necrosis, cell membrane rupture, etc., to improve survival rate, leave no scars, trauma and pain less effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0023] Example 1 Extraction, purification and culture of autologous adipose stem cells
[0024] (1) After removing the excess tissues such as blood vessels in the obtained fat tissue (30 ml),
[0025] Rinse 2-3 times with antibiotic D-PBS (American Sigma Company);
[0026] (2) Add 2mg / ml type I collagenase to the washed fat (Worthington, USA)
[0027] Company) digested at 37°C for 60-90 min, complete medium (DMEM+10% FBS, all from Gibco, USA) to terminate the digestion
[0028] (3) 200 mesh screen filters the digested products of human adipose tissue;
[0029] (4) After filtering, centrifuge at 1500 rpm for 10 min, resuspend in complete medium,
[0030] Trypan blue (China National Pharmaceutical Group) is counted after dyeing;
[0031] (5) 1×10 5 / cm 2 Inoculate human adipose stem cells in
[0032] In a T25 plastic culture bottle (Corning, USA), and place it in a 37°C, 5% carbon dioxide incubator;
[0033] (6) When the human adipose stem cells grow to about 85%, cell passage is carried out. ...
Example Embodiment
[0038] Example 2 Using the breast repair material of the present invention for breast augmentation
[0039] (1) The patient was 62 years old, and 100 ml of adipose tissue was extracted from the patient, and adipose stem cells were extracted, purified, and cultured according to Example 1.
[0040] (2) After the first adipose tissue extraction, after 40 days for the second liposuction operation, 550ml adipose tissue was obtained. The adipose tissue was washed, centrifuged at a low speed, deoiled and watered, and fibrous connective tissue was removed in the laboratory. , To obtain complete fat particles.
[0041] (3) Collect the adipose stem cells cultured in step (1) and mix them evenly into the fat particles obtained in step (2) to obtain an injectable compound.
[0042] (4) The injectable compound obtained in step (3) is injected into the fat tissue, posterior breast space, and subcutaneous tissue of the patient's breast by the plastic surgeon through multiple tunnels and multiple lev...
Example Embodiment
[0045] Example 3 Application of the breast repair material of the present invention to breast asymmetric repair
[0046] (1) The patient was 41 years old, and 80 ml of the patient's adipose tissue was extracted, and the adipose stem cells were extracted, purified, and cultured according to Example 1.
[0047] (2) After the first adipose tissue extraction, a second liposuction operation was performed after 26 days to obtain 300ml adipose tissue. The adipose tissue was washed, centrifuged at a low speed, deoiled and watered, and fibrous connective tissue was removed in the laboratory. , To obtain complete fat particles.
[0048] (3) Collect the adipose stem cells cultured in step (1) and mix them evenly into the fat particles obtained in step (2) to obtain an injectable compound.
[0049] (4) The injectable compound obtained in step (3) is injected into the fat tissue, posterior breast space, and subcutaneous tissue of the patient's breast by the plastic surgeon through multiple tunnels...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap