Phosphating agent used before high-speed drawing of steel wires and preparation method for phosphating agent

A phosphating agent, high-speed technology, applied in the field of phosphating agent, can solve problems affecting production efficiency, achieve the effects of improving production efficiency, high lubrication and wear resistance, and preventing steel wire from breaking

Inactive Publication Date: 2012-01-04
DALIAN SANDAAOKE CHEM
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] However, the phosphating agent currently used in the steel wire drawing process can only form a phosphating film that can meet the drawing speed of 10-12 m / s, which seriously affects the production efficiency

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0024] The embodiment of the present invention is a phosphating agent for steel wire before high-speed drawing, including a build-up agent and a supplement, and is characterized in that:

[0025] The raw materials and mass ratio of the described tank building agent are as follows (in 1000 kg):

[0026] Phosphoric acid with a concentration of 85% 130 ~ 150kg

[0027] Nitric acid 110 ~ 140 kg

[0028] Zinc oxide (99.98%) 100 ~ 130 kg

[0029] Nickel nitrate 3 ~ 6 kg

[0030] water balance.

[0031] The raw materials and mass ratio of the supplement are as follows (in 1000 kg):

[0032] Phosphoric acid with a concentration of 85% 260 ~ 320 kg

[0033] Nitric acid 65 ~ 95 kg

[0034] Zinc oxide (99.98%) 100 ~ 130 kg

[0035] Nickel nitrate 1~4 kg

[0036] water balance.

[0037] The specific dosage of various raw materials of the tank building agent and supplement can be selected within the above quality range according to the phosphating process parameters. Phosphating...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a phosphating agent used before high-speed drawing of steel wires and a preparation method for the phosphating agent. The phosphating agent can improve the drawing speed, prevent the steel wires from being broken and ensure that the surfaces of the drawn steel wires are smooth and uniform. The phosphating agent comprises a tank building agent and a supplementing agent, wherein the tank building agent comprises the following raw materials in percentage by mass: 13 to 15 percent of phosphoric acid at the concentration of 85 percent, 11 to 14 percent of nitric acid, 10 to 13 percent of zinc oxide, 0.3 to 0.6 percent of nickel nitrate, and the balance of water; and the supplementing agent comprises the following raw materials in percentage by mass: 26 to 32 percent of phosphoric acid at the concentration of 85 percent, 6.5 to 9.5 percent of nitric acid, 10 to 13 percent of zinc oxide, 0.1 to 0.4 percent of nickel nitrate, and the balance of water.

Description

technical field [0001] The invention relates to a phosphating agent, in particular to a phosphating agent for steel wire before high-speed drawing, which can increase the drawing speed, prevent the steel wire from being broken, and ensure that the surface of the drawn steel wire is smooth and uniform, and a preparation method thereof. Background technique [0002] The steel workpiece is chemically treated in a phosphate solution containing Zn, Mn, and Fe, and the process of depositing a layer of crystalline phosphate conversion film that is insoluble in water on its surface is called phosphating. The phosphating film has many functions, among which it has been widely used as the bottom layer for cold pier, cold extrusion and lubrication during drawing of steel workpieces. Taking the phosphating film before drawing as an example, its main functions are as follows: [0003] (1) Since the lubricant is adsorbed on the bottom layer of the phosphating film, friction can be reduce...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23C22/13
Inventor 潘德顺张礼让朱宏龚瑞何成利
Owner DALIAN SANDAAOKE CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap