Antistatic stone paper for packing

A technology for stone paper and packaging, applied in the direction of fibrous fillers, dyed polymer organic compounds, etc., can solve the problems of white pollution, natural resource consumption, environmental pollution, etc.

Active Publication Date: 2012-02-29
山东高旭新材料有限公司
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Because traditional packaging paper is made of wood fiber base paper, the consumption of energy and natural resources is conceivable, and it also causes serious pollution to the environment.
Although the antistatic plastic film has achieved a ce...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antistatic stone paper for packing
  • Antistatic stone paper for packing
  • Antistatic stone paper for packing

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] 1. 3 parts of glycerol, 0.5 part of 6-nitrobenzimidazole nitrate, 0.5 part of potassium nitrate, 1 part of polytetrafluoroethylene micropowder, 0.4 part of bisphenol A, 2 parts of antistatic agent, 90 parts of heavy calcium carbonate 1 part of barium stearate, 2 parts of silane coupling agent, 5 parts of butyl acrylate, 0.075 parts of dimethyl azobisisobutyrate, 15 parts of linear low density polyethylene, 10 parts of hot melt adhesive, erucic acid 0.5 parts of amide, 0.5 parts of stearic acid, 1.5 parts of dioctyl epoxy tetrahydrophthalate, 1.5 parts of dioctyl sebacate, 0.6 parts of polyethylene wax, and 0.5 parts of sorbitan stearate.

[0024] 2. The preparation process of antistatic stone paper for packaging. First, prepare functional calcium carbonate for stone paper. The preparation process is as follows: a. Fully dissolve potassium nitrate in glycerin, and then dilute with absolute ethanol twice the weight of the solution Finally, add 6-nitrobenzimidazole nitrate...

Embodiment 2

[0027] 1. 4 parts of glycerol, 1 part of 6-nitrobenzimidazole nitrate, 0.75 parts of potassium nitrate, 2 parts of polytetrafluoroethylene micropowder, 0.5 parts of bisphenol A, 3 parts of antistatic agent, 90 parts of heavy calcium carbonate 1.5 parts of barium stearate, 3 parts of silane coupling agent, 6 parts of methyl acrylate, 0.12 parts of tert-butyl peroxybenzoate, 11 parts of linear low density polyethylene, 6 parts of hot melt adhesive, erucic acid 1 part of amide, 1 part of stearic acid, 1 part of dioctyl epoxy tetrahydrophthalate, 1 part of dioctyl sebacate, 0.4 part of polyethylene wax, 0.6 part of sorbitan stearate.

[0028] 2. The preparation process of antistatic stone paper for packaging. First, prepare functional calcium carbonate for stone paper. The preparation process is as follows: a. Fully dissolve potassium nitrate in glycerin, and then use absolute ethanol twice the weight of the solution After dilution, add 6-nitrobenzimidazole and nitrate, fully diss...

Embodiment 3

[0031] 1. 5 parts of glycerol, 0.75 parts of 6-nitrobenzimidazole nitrate, 1 part of potassium nitrate, 3 parts of polytetrafluoroethylene micropowder, 0.6 parts of bisphenol A, 4 parts of antistatic agent, 95 parts of heavy calcium carbonate 2 parts of barium stearate, 4 parts of silane coupling agent, 7 parts of vinyl acetate, 0.15 parts of dimethyl azobisisobutyrate, 12 parts of linear low density polyethylene, 7 parts of hot melt adhesive, erucic acid 1.5 parts of amide, 1.5 parts of stearic acid, 1.5 parts of dioctyl epoxy tetrahydrophthalate, 1.5 parts of dioctyl sebacate, 0.6 parts of polyethylene wax, and 0.7 parts of sorbitan stearate.

[0032] 2. The preparation process of antistatic stone paper for packaging. First, prepare functional calcium carbonate for stone paper. The preparation process is as follows: a. Fully dissolve potassium nitrate in glycerin, and then dilute with absolute ethanol twice the weight of the solution Finally, add 6-nitrobenzimidazole nitrate...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides antistatic stone paper for packing and a preparation method of the antistatic stone paper. The antistatic stone paper for packing comprises the following components in parts by weight: 3 to 5 parts of glycerol, 85 to 95 parts of heavy calcium carbonate, 1 to 2 parts of barium stearate, 1 to 3 parts of polytetrafluoroethylene micro powder, 2 to 4 parts of antistatic agent, 2to 4 parts of silane coupling agent, 5 to 10 parts of functional monomer, 10 to 15 parts of linear low density polyethylene, 5 to 10 parts of hot melt adhesive, and 1 to 3 parts of epoxy tetrahydrodioctyl phthalate. The resistance of the surface of the paper can be reduced, the generated static electricity is immediately neutralized, the conditions of generating static electricity due to frictionin the production process and the use process of the stone paper are inhibited, various harms caused by static electricity are effectively prevented, and the potential safety hazard is eliminated.

Description

technical field [0001] The invention relates to an antistatic stone paper. Background technique [0002] With the rapid development of the economy and the continuous improvement of people's material living standards, people's requirements for material and cultural life are also getting higher and higher. High-quality, high-grade products require excellent packaging services, thus promoting the vigorous development of the packaging industry . Various precision instruments, household electrical appliances, fine chemical raw materials, and hazardous chemicals demand more and more packaging paper. Today's world has entered the information age, and electromagnetic waves of various wavelengths are filling every corner of the earth. Various electromagnetic waves have certain interference and damage to unshielded sensitive electronic components, which can easily cause data distortion and information confusion; various precision Instruments, household appliances, fine chemical raw ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/08C08K13/06C08K3/26C08K5/20C08K5/103C09C1/02C09C3/10
Inventor 施晓旦郭和森王养臣
Owner 山东高旭新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap