Wrinkle-resistant shape-retaining shell fabric

A wrinkle-preserving and fabric-preserving technology, which is applied in fabrics, textiles, textiles, and papermaking, can solve the problems of poor anti-wrinkle and shape-retaining performance, poor comfort compared with pure cotton fabrics, and incomparable hand feeling with pure cotton fabrics. Good anti-wrinkle performance, good hand feeling effect, light specific gravity effect

Inactive Publication Date: 2012-06-13
DALIAN DEDA TECH DEV
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, pure cotton fabrics have poor anti-wrinkle and shape-retaining properties due to their raw materials being natural fibers.
Although polyester-cotton fabrics have bet

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Wrinkle-resistant shape-retaining shell fabric
  • Wrinkle-resistant shape-retaining shell fabric
  • Wrinkle-resistant shape-retaining shell fabric

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0009] In order to understand the structure of an anti-wrinkle and conformal fabric, combine figure 1 , figure 2 described as follows:

[0010] A kind of anti-wrinkle shape-retaining fabric woven by warp 1 and weft 2, warp 1 is multifilament, weft 2 is monofilament, warp 1 and weft 2 are woven into a 3 / 1 1 / 3 composite structure; warp 1 uses Long-staple cotton and 0.8dtex×38mm superfine polyester blended multifilament, the specification of the multifilament is 100S / 3, the weft 2 adopts polypropylene monofilament, and the specification of the monofilament is 0.4 mm in diameter. The multifilament is concentrated on the upper surface of the fabric, and the monofilament is concentrated on the lower surface of the fabric, and forms a horn-shaped hole with a smooth surface and large upper and lower surfaces.

[0011] The monofilament is interwoven, and the multifilament is completely floating on the entire cloth surface, which has a good hand feeling. When the material enters the fab...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A wrinkle-resistant shape-retaining shell fabric relates to the textile field and is interwoven with multifilaments and monofilaments. The multifilaments completely float on the whole fabric surface so that good touch is achieved. When a material enters the fabric, the monofilaments fully occupying the interior of the fabric are high in wrinkle resistance. The wrinkle-resistant shape-retaining shell fabric has the advantages of low monofilament fineness, light specific gravity, high rupture resistance, high elongation at rupture, high glossiness, high moisture absorption and permeability and the like, has clothing performances such as wool-like touch, silk-like softness and gloss, moisture absorption and permeability as cotton fibers, heat preservation as wool and the like, and meets requirements and needs of people on wearing comfort and functionality of clothing supplies. The wrinkle-resistant shape-retaining shell fabric made by domestic universal cotton spinning processes is crystal comfortable, likes cotton cloth and chemical fibers, is super comfortable to touch and is wrinkle-resistant and shape-retaining.

Description

technical field [0001] The invention relates to a wrinkle-resistant and shape-retaining fabric, which relates to the field of textiles. Background technique [0002] At present, because the raw material of pure cotton fabrics is natural fibers, its anti-wrinkle and shape-retaining properties are very poor. Although polyester-cotton fabrics have better anti-wrinkle and shape-retaining properties, their comfort is not as good as that of pure cotton fabrics, and they cannot be compared with pure cotton fabrics in terms of feel. Contents of the invention [0003] In view of the defects in the prior art, the object of the present invention is to provide a wrinkle-resistant and shape-retaining fabric with crystal-like comfort, chemical fiberization of cotton cloth, super-Q hand feeling, and wrinkle-resistance and shape retention. [0004] In order to achieve the above object, the technical solution adopted in the present invention is: a kind of anti-wrinkle and shape-preser...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D03D15/00D03D13/00D02G3/04D03D15/217D03D15/283D03D15/47D03D15/50D03D15/547D03D15/573
Inventor 李霞
Owner DALIAN DEDA TECH DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap