Glass mosaic for advertisement

A technology for glass mosaic and advertising, applied in the field of mosaic, can solve the problems of poor color fixing performance and high cost of mosaic

Inactive Publication Date: 2012-06-20
SHANGHAI JIAHUA ADVERTISEMENT
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the cost of existing mosaics is relatively high, and the color fixing performance is not good

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] (1) Weigh out:

[0021] Glass powder 100 kg;

[0022] Quartz sand 10 kg;

[0023] Kaolin 4 kg;

[0024] Sodium ferric pyrophosphate 0.2 kg;

[0025] albite 1.5 kg;

[0026] Ferric orthophosphate 0.1 kg;

[0027] 2 kg of starch;

[0028] Inorganic Pigment 0.2 kg.

[0029] Stir and mix the above components evenly, add an appropriate amount of water, pressurize to 25-30Mpa with a press, press and shape, sinter in a kiln for 30-35 minutes, the maximum temperature is 850 ° C, hold for 2-4 minutes, and anneal. After cooling, the advertising glass mosaic of the present invention can be obtained.

Embodiment 2

[0031] (1) Weigh out:

[0032] Glass powder 100 kg;

[0033] Quartz sand 20 kg;

[0034] Kaolin 1 kg;

[0035] Sodium ferric pyrophosphate 0.4 kg;

[0036] albite 0.5 kg;

[0037] Ferric orthophosphate 0.3 kg;

[0038] 1 kg of starch;

[0039] Inorganic Pigment 0.8 kg.

[0040] Stir and mix the above components evenly, add an appropriate amount of water, pressurize to 25-30Mpa with a press, press and shape, sinter in a kiln for 30-35 minutes, the maximum temperature is 850 ° C, hold for 2-4 minutes, and anneal. After cooling, the advertising glass mosaic of the present invention can be obtained.

[0041] The advertising glass mosaic of the invention has the advantages of low cost, little radioactivity, safe use and excellent color-fixing performance.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a glass mosaic for advertisement, comprising the components in parts by weight as follows: 100 parts of glass powder, 10-20 parts of quartz sand, 1-4 parts of kaolin, 0.2-0.4 parts of sodium ferric pyrophosphate, 0.5-1.5 parts of albite, 0.1-0.3 parts of ferric orthophosphate, 1-2 parts of starch and 0.2-0.8 parts of inorganic pigment. The glass mosaic for advertisement provided by the invention has a low cost, small radioactivity and excellent color fixing performance and is safe to use.

Description

technical field [0001] The invention relates to a mosaic, in particular to a glass mosaic for advertising. Background technique [0002] Mosaic (Mosaic), the architectural term is mosaic, divided into two types: ceramic mosaic and glass mosaic. It is a decorative art that usually uses many small stones or fragments of colored glass to form a pattern. The glass art in the church is also called stained glass. In the era of the Byzantine Empire, with the rise of Christianity, mosaics developed into the form of frescoes in churches and palaces. Mosaic today generally refers to this type of colorful visual effect. Mosaic is divided into ceramic mosaic tiles and glass mosaic tiles. It is a decorative art that usually uses many small stones or fragments of colored glass to form a pattern. The glass art in the church is also called stained glass. In the era of the Byzantine Empire, with the rise of Christianity, mosaics developed into the form of frescoes in churches and palaces...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine