Cement based penetration crystallization type waterproof material

A technology for infiltrating crystalline and waterproof materials, applied in the field of cement-based infiltrating crystalline waterproof materials, can solve problems such as the performance and poor performance of waterproof coatings, and achieve the effects of inhibiting bacterial growth, simple operation and good wear resistance.

Inactive Publication Date: 2012-06-27
江门市蓬江区智远防水建材有限公司
View PDF1 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The purpose of the present invention is to solve the long-term problem of leakage that has plagued people and the problem of poor performance of existing waterproof coatings. The waterproof material of the present invention has good cohesiveness, water resistance and air permeability, and can overcome the problems of cement in the prior art. Based on the shortcomings of permeable crystalline waterproof materials, it is suitable for large-scale promotion and application, and has significant economic and social benefits

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A cement-based permeable crystalline waterproof material described in Example 1 of the present invention is composed of silicate cement, quartz sand, silica micropowder, water-repellent agent and cellulose.

[0030] The aforementioned ordinary Portland cement is 42.5R ordinary Portland cement; the particle size of the quartz sand is 100-200 mesh; the silicon micropowder is 800-1200 mesh; Said cellulose adopts methyl cellulose ether. According to the percentage by weight, it is specifically: 57% of 42.5R ordinary Portland cement, 37% of quartz sand, 5% of silica powder, 0.18% of water repellent, and 0.82% of methyl cellulose ether. The above components are evenly mixed.

[0031] Weigh each component according to the weight ratio, add ordinary Portland cement, quartz sand, silicon micropowder, water repellent, and cellulose into the mixing tank, fully stir and mix evenly, and stir for 25 minutes to 35 minutes.

Embodiment 2

[0033] A cement-based permeable crystalline waterproof material described in Example 2 of the present invention is composed of silicate cement, quartz sand, silica micropowder, water-repellent agent and cellulose. The aforementioned ordinary Portland cement is 42.5R ordinary Portland cement; the particle size of the quartz sand is 100-200 mesh; the silicon micropowder is 800-1200 mesh; Said cellulose adopts methyl cellulose ether. According to the percentage by weight, it is specifically: 42.5R ordinary Portland cement 55%, quartz sand 38%, silica micropowder (%), water reducing agent 0.17%, methyl cellulose ether 1.83%, and the above components are mixed evenly.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to view more

Abstract

The invention discloses a cement based penetration crystallization type waterproof material, which is prepared from the following substances of: by weight, 1% of portland cement, 0.6-0.7% of quartz sand, 0.08-0.1% of silicon powder, 0.002-0.003% of a water repellent and 0.005-0.1% of cellulose. The waterproof material provided by the invention has good caking property, waterproofness and permeability, can overcome disadvantages of a cement based penetration crystallization type waterproof material in the prior art, is suitable for large-scale popularization and application, and has substantial economic benefits and social benefits.

Description

technical field [0001] The invention relates to a cement-based permeable crystalline waterproof material, which is a novel cement-based permeable crystalline waterproof material. Background technique [0002] Since the national standard "GB18445 (2001) Cement-based permeable crystalline waterproof material" was implemented on March 1, 2002, it has promoted the research and development and engineering application of this material, improved the work efficiency of waterproof engineering, and reduced the comprehensive cost of waterproof engineering ; To some extent, it meets the durability requirements of modern buildings. It can be said that the cement-based permeable crystalline waterproof material has won the favor of people from all walks of life with its comprehensive advantages, and has established its important position in the series of rigid waterproof materials and plugging and water-stopping materials. [0003] The research and engineering application of foreign cemen...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04
Inventor 梁智颖
Owner 江门市蓬江区智远防水建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap