Method for producing austempered ductile iron (ADI) cylinder sleeve

A production method and cylinder liner technology, which are applied in the field of ADI supercharged engine cylinder liner and production, can solve the problems of energy waste, fatigue performance and wear resistance that cannot meet the requirements of high-enhanced engine service, and poor emission indicators.

Active Publication Date: 2014-03-05
扬州华铁机电集团有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Such bad emission indicators have seriously affected the environment and caused a waste of energy.
[0003] Materials currently in service: boron cast iron, boron-copper cast iron, chrome-molybdenum-copper cast iron, high-phosphorus alloy cast iron, high-phosphorus cast iron, high-content chromium-molybdenum-nickel cast iron, and chromium-molybdenum-copper-boron alloy cast iron. Requirements for Strengthening Engine Service

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for producing austempered ductile iron (ADI) cylinder sleeve
  • Method for producing austempered ductile iron (ADI) cylinder sleeve

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] 1. Production steps:

[0016] 1. Pouring ADI cylinder liner slab:

[0017] Select synthetic cast iron or high-purity nodular iron pig iron carbonized by scrap steel as the main metal material for the production of ADI cylinder liners, and strictly control the addition of alloying elements; melt molten iron in an intermediate frequency electric furnace, purify the molten iron by blowing argon; 1480 ~ 1560 ° C, Spheroidization treatment and secondary inoculation treatment are adopted.

[0018] Addition of alloying elements (%), the rest is Fe:

[0019] C Si mn P S Mg Re 3.1-3.9 2.0-3.0 ＜0.31 ＜0.03 ＜0.02 0.039-0.062 ≥0.02

[0020] 2. Analysis: The number of graphite nodules of the formed ADI (rare earth Aubey ductile iron) cylinder liner slab is grade 1-4 of GB9441-88; the size of graphite is grade 5 not thicker than GB9441-88; the matrix structure The total amount of medium phosphorus eutectic cementite is ≤5%; the ratio of pearlite and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
hardnessaaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for producing an austempered ductile iron (ADI) cylinder sleeve, belongs to metal materials, and in particular relates to the technical field of production processes for ADI supercharged engine cylinder sleeves. The method comprises the steps of casting an ADI cylinder sleeve casting blank, finely machining the cylinder sleeve casting blank, performing isothermal quenching treatment and shot blasting treatment and machining platform reticulate patterns. The method solves the problem that the fatigue property and the abrasion resistance of the conventional service materials such as boron cast iron, boron-copper cast iron, chromium-molybdenum-copper cast iron, high-phosphorus alloy cast iron, high-phosphorus cast iron, high-content chromium-molybdenum-nickel cast iron and chromium-molybdenum-copper-boron alloy cast iron cannot meet the service requirements of high strength engines.

Description

Technical field [0001] The present invention involves metal materials, which specializes in an ADI (equivalent temperature quenching iron) supercharged engine air cylinder set and production technology field. Background technique [0002] In existing technologies, the engine gas cylinder set is manufactured by boron cast iron, boron copper cast iron, chromium molybdenum copper cast iron, high phosphorus alloy cast iron, high phosphorus cast iron, high -content chromium molybdenum nickel cast iron, chromium molybdenum copper boron alloy cast iron.The surface hardening treatment of the cylinder sleeve body uses hot treatment processes such as soft nitrogen, laser, high -frequency quenching, chrome -plated surface, or the inner surface of the body (hardness HB207 ~ 360) with platform polishing mesh or soft nitrogen (only 0.030mm in the synthetic layer of the compound layer) The back platform is polished. When the surface hardening layer is ground, the inside of the inside of the cyl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23P15/00
Inventor 徐志富臧权同王克宇徐帅
Owner 扬州华铁机电集团有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com