Calcium magnesium phosphate for ceramic and preparation method thereof

A technology of calcium magnesium phosphate and production method, which is applied in chemical instruments and methods, phosphorus compounds, inorganic chemistry, etc., can solve the problems of reducing the ornamental value of products and single color, and achieve stable glaze color, good thermal stability, and delicate enamel surface smooth effect

Active Publication Date: 2012-07-04
淄博华光国瓷科技文化有限公司
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the porcelain made from animal ashes can only be white and has a single color, which reduces the ornamental value of the product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Ca(OH) 2 , MgCO 3 by weight Ca 2+ : Mg 2+ = 7: 3 ratio mixing, adding to the reaction device at the same time, adding water to dilute, stirring for 20-30min, making solution A for later use;

[0024] Weigh phosphoric acid according to the molar ratio of Ca+Mg / P=1.15, pour it into a stainless steel container with water in a volume ratio of 1:1.5, and dilute it into solution B with a concentration of 30% for later use;

[0025] Slowly titrate solution B into solution A to make it react evenly. The specific reaction formula is:

[0026] MgCO 3 +Ca(OH) 2 +H 3 PO 4 -→ Ca 2 Mg(PO 4 ) 2 +H 2 O+CO 2

[0027] MgCO 3 +Ca(OH) 2 +H 3 PO 4 -→CaMg(HPO 4 ) 2 +H 2 O+CO 2

[0028] After the reaction, the pH of the solution = 6, let it stand for 3 to 10 hours to obtain MgCa 2 (PO 4 ) 2 and CaMg(HPO 4 ) 2 The solution C of solution C is press-filtered and dried to obtain a filter cake with a water content of less than 10%;

[0029] The filter cake is calcined u...

Embodiment 2

[0035] Ca(OH) 2 , MgCO 3 by weight Ca 2+ : Mg 2+ = 6:4 ratio mixing, adding to the reaction device at the same time, and adding water to dilute, stirring for 20-30min to make solution A;

[0036] Weigh phosphoric acid according to the molar ratio of Ca+Mg / P=1.2, pour it into a stainless steel container with water in a volume ratio of 1:2, and dilute it to a solution B with a concentration of 25%;

[0037] Slowly titrate solution B into solution A to make the reaction uniform. After the reaction, the pH of the solution is 7, and let it stand for 3 to 10 hours to obtain MgCa 2 (PO 4 ) 2 and CaMg(HPO 4 ) 2 The solution C of solution C is press-filtered and dried to obtain a filter cake with a water content of less than 10%;

[0038] The filter cake is calcined under an oxidizing flame at 20-1260°C for 14-16 hours, then calcined at a weak reducing flame at 1260-1300°C for 2-3 hours, and after cooling, calcium magnesium phosphate salt is obtained.

[0039] Reaction princip...

Embodiment 3

[0041] Ca(OH) 2 , MgCO 3 by weight Ca 2+ :Mg 2+= 8:2 ratio mixing, adding to the reaction device at the same time, adding water to dilute, stirring for 20-30min, to make solution A;

[0042] Weigh phosphoric acid according to the molar ratio of Ca+Mg / P=1.3, pour it into a stainless steel container with a volume ratio of 1:1.75 with water, and dilute it into solution B with a concentration of 35%;

[0043] Slowly titrate solution B into solution A to make the reaction uniform. After the reaction, the pH of the solution is 5, and let it stand for 3 to 10 hours to obtain MgCa 2 (PO 4 ) 2 and CaMg(HPO 4 ) 2 The solution C of solution C is press-filtered and dried to obtain a filter cake with a water content of less than 10%;

[0044] The filter cake is calcined under an oxidizing flame at 20-1260°C for 14-16 hours, then calcined at a weak reducing flame at 1260-1300°C for 2-3 hours, and after cooling, calcium magnesium phosphate salt is obtained.

[0045] Reaction princip...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method of calcium magnesium phosphate for ceramic, belonging to the field of ceramic glass materials. The calcium magnesium phosphate for ceramic is characterized in that the calcium magnesium phosphate for ceramic is synthesized by using phosphoric acid, calcium hydroxide and magnesium carbonate through chemical reaction, and the chemical compositions of the calcium magnesium phosphate comprise MgCa2(PO4) and CaMg(HPO4)2, wherein the weight ratio of Ca<2> to Mg<2> is (6-9): (1-4). A ceramic product made of the calcium magnesium phosphate for ceramic which is used as a main material has the advantages that the ceramic glaze surface is fine and smooth, the glazing color is stable, nontoxic and environmental-friendly and the application scope is wide. By introducing a large quantity of magnesium oxide to replace partial calcium oxide, the produced ceramic product has the advantages that the entire body has light-blue gloss, the semi-transparency is higher, the refraction principle of light can be fully utilized, and the ceramic product is enabled to have attractive gloss with white in blue and blue in white.

Description

technical field [0001] A calcium magnesium phosphate salt for ceramics and a preparation method thereof belong to the field of ceramic glass materials. Background technique [0002] Raw materials such as clay, feldspar, and quartz are the main components in the production of traditional porcelain. Porcelain fired with traditional raw materials has a single type of color and poor ornamental value. With the continuous improvement of people's living standards, the environmental protection and decoration of daily-use ceramic products have attracted much attention, especially some high-grade porcelains are more and more popular because of their clear porcelain and beautiful color. At present, many new varieties of daily-use ceramics have emerged, such as Luyu porcelain, steatite porcelain, high-quartz porcelain and bone china. development is gradually enriched. [0003] At present, the main components of high-grade ceramics are not limited to basic raw materials such as clay, f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C01B25/45C04B35/447
Inventor 孟莉张宁陈娜
Owner 淄博华光国瓷科技文化有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com