Production process of nano titanium tussah silk fiber anti-electromagnetic textile yarns

A technology of textile yarn and production process, which is applied in the field of production technology of nano-titanium tussah silk fiber anti-electromagnetic textile yarn, can solve the problem of no radiation protection function and the like, and achieve the effect of reducing damage and reducing the probability of cancer

Inactive Publication Date: 2012-07-04
XIAN ZONGHENG TEXTILE TECH
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The purpose of the present invention is to propose a production process of nano-titanium tussah silk fiber anti-electromagnetic textile yarn, which solves the problem that tussah silk fibers commonly used do not have anti-radiation functions, and further increases the usage of tussah silk fibers and the scope of application. wider

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] 1. Preparation of padding solution: the substances and dosages in the padding solution are titanium powder (30-60nm) 30g / L, penetrant JFC 2ml / L, fixing agent WLS 20g / L, binder BH 15g / L, NaOH 3g / L . Among them, the binder and the fixing agent are added first, and then the titanium powder is added after stirring evenly;

[0017] 2. Padding: adopt the method of two dips and two rolls, roll speed: 2r / min, roll pressure: 0.08Mpa;

[0018] 3. Drying: drying at 100℃ for 12min;

[0019] 4. Baking: Bake at 130℃ for 4min.

Embodiment 2

[0021] 1. Preparation of padding solution: the substances and dosages in the padding solution are titanium powder (30-60nm) 35g / L, penetrant JFC 3ml / L, fixing agent WLS 25g / L, binder BH 20g / L, NaOH 4g / L . The order of adding is the same as that of Embodiment 1;

[0022] 2. Padding: adopt the method of two dips and two rolls, roll speed: 2.5r / min, roll pressure: 0.1Mpa;

[0023] 3. Drying: drying at 105℃ for 10min;

[0024] 4. Baking: Bake at 140℃ for 3min.

Embodiment 3

[0026] 1. Preparation of padding solution: The substances and dosages contained in the padding solution are titanium powder (30-60nm) 40g / L, penetrant JFC 5ml / L, fixing agent WLS 30g / L, binder BH 25g / L, NaOH 5g / L . The order of adding is the same as that of Embodiment 1;

[0027] 2. The method of two dips and two rollings is adopted, the roll speed: 3r / min, the roll pressure: 0.12Mpa;

[0028] 3. Drying: drying at 110℃ for about 8min;

[0029] 4. Baking: Bake at 150℃ for 2min.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a production process of nano titanium tussah silk fiber anti-electromagnetic textile yarns. In the production of the titanium tussah silk fiber anti-electromagnetic textile yarns, a padding liquid with optimal components and optimal concentration is prepared by using nano titanium powder and artificially synthesized fixative WLS, the padding liquid is applied on the tussah silk fiber by adopting a double-dip-double-nip manner, and the fixation effect of the titanium powder on the tussah silk fiber is enhanced by adopting an optimal baking process. The produced nano titanium tussah silk fiber radiation-resistant composite yarns have the titanium powder content more than 30%; the product produced from the yarns has a good radiation protection effect; and the product prepared from the radiation-resistant composite titanium tussah silk fiber produced by the production process satisfies the radiation protection requirement of people.

Description

technical field [0001] The invention relates to a production process of a nanometer titanium tussah silk fiber anti-electromagnetic textile yarn, and the composite titanium tussah silk fiber has good radiation protection function. Background technique [0002] Entering the information age, electromagnetic radiation is an "invisible killer" that people often overlook. , telecommunications, civil aviation, railways, medical and other eight industries are high-risk industries prone to electromagnetic radiation pollution. In addition, the electromagnetic radiation of various electrical appliances in the living environment is not easy to ignore, among which the electromagnetic radiation of microwave ovens, computers and mobile phones has reached 200 milligauss (mgs). and children are even more at risk. The main symptoms are headache, dizziness, memory loss, decreased concentration, depression, irritability, etc. For some people with electromagnetic sensitivity, it will also cau...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06M11/83D06M101/12
Inventor 李小龙
Owner XIAN ZONGHENG TEXTILE TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com