Composite fire-proof insulation board and preparation method thereof

A technology of fireproof insulation board and composite materials, which is applied in the manufacture of tools, ceramic molding machines, etc., can solve the problems of long maintenance time and unfavorable mass production, etc., and achieve the effect of high early strength, shortened maintenance time and excellent performance

Inactive Publication Date: 2012-07-18
NANJING TIANYA NEW MATERIALS
View PDF3 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Existing fire-proof insulation boards are directly paved and formed after mixing and stirring the raw materials. Usually, excessive water is required to prepare a thin slurry for wet forming. At the same time, the curing time is long, which is not conducive to mass production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] (1) Mixed raw materials: take 30kg of cement, 20kg of fly ash, and 0.2m of vitrified microbeads 3 , EPS particles 0.7 m 3 Put 0.2kg of methyl cellulose into the blender and stir for 2 minutes;

[0016] (2) Preparation of slurry: Add 80.2 kg of water to the raw material stirred evenly in step (1), and stir evenly for 1.5 minutes to form a slurry;

[0017] (3) Molding: Use a composite material molding machine to mold the slurry prepared in step (2) on the bottom mold at a molding speed of 3.5m 2 / minute;

[0018] (4) Curing: Curing the slurry formed in step (3) at 60°C for 8 hours;

[0019] (5) Demoulding: After curing, remove the bottom mold to obtain the product.

Embodiment 2

[0021] (1) Mixed raw materials: take 80kg of cement, 60kg of fly ash, and 0.7m of vitrified microbeads 3 , EPS particles 0.7 m 3 Put 1kg of methyl cellulose into the blender and stir for 2 minutes;

[0022] (2) Preparation of slurry: Add 246kg of water to the raw material stirred evenly in step (1), and stir evenly for 1.5 minutes to form a slurry;

[0023] (3) Molding: Use a composite material molding machine to shape the slurry prepared in step (2) on the bottom mold at a molding speed of 4.5m 2 / minute;

[0024] (4) Curing: Curing the slurry formed in step (3) at 80°C for 12 hours;

[0025] (5) Demoulding: After curing, remove the bottom mold to obtain the product.

Embodiment 3

[0027] (1) Mixed raw materials: take 65kg of cement, 50kg of fly ash, and 0.6m of vitrified microbeads 3 , EPS particles 0.6 m 3 Put 0.8kg of methyl cellulose into the mixer and stir for 2 minutes;

[0028] (2) Preparation of slurry: Add 205.8 kg of water to the raw material stirred evenly in step (1), and stir evenly for 1.5 minutes to form a slurry;

[0029] (3) Molding: use a composite material molding machine to mold the slurry prepared in step (2) on the bottom mold at a molding speed of 4m 2 / minute;

[0030] (4) Curing: Curing the slurry formed in step (3) at 70°C for 10 hours;

[0031] (5) Demoulding: After curing, remove the bottom mold to obtain the product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
water absorptionaaaaaaaaaa
Login to View More

Abstract

The invention discloses a composite fire-proof insulation board and a preparation method thereof. The composite fire-proof insulation board is prepared from the raw materials of 30-80kg of cement, 20-60kg of coal ash, 0.2-0.7m<3> of glazed hollow beads, 0.2-0.7m<3> of expandable polystyrene (EPS) particles, 0.2-1kg of methylcellulose and water, wherein, the weight of the water accounts for 50% of the weight of the raw materials. The composite fire-proof insulation board provided by the invention is characterized by short curing time and high early strength.

Description

technical field [0001] The invention specifically relates to a composite material fireproof insulation board and a preparation method thereof. Background technique [0002] Existing fireproof insulation boards are directly paved and formed after mixing and stirring raw materials. Usually, excessive water is required to prepare dilute slurry for wet forming. At the same time, the curing time is long, which is not conducive to mass production. Contents of the invention [0003] The purpose of the present invention is to solve the defects in the prior art, and provide a composite material fireproof insulation board with short curing time and a preparation method thereof. [0004] In order to achieve the above purpose, the present invention provides a composite material fire-proof insulation board, which is composed of the following raw materials: 30-80kg of cement, 20-60kg of fly ash, 0.2-0.7m vitrified beads 3 , EPS (expandable polystyrene) particles 0.2~0.7 m 3 , ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00B28B1/52B28B1/14
Inventor 缪建华
Owner NANJING TIANYA NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com