Method for preparing ultrafine inorganic powder dispersion
A technology of inorganic powder and inorganic powder material, which is applied in the direction of dyeing polymer organic compound treatment, fibrous filler, dyeing physical treatment, etc., to achieve the effect of preventing mutual aggregation, simple operation and wide adaptability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0028]20g of epoxy resin prepolymer (E44, Baling Petrochemical) was added into 20g of acetone and stirred and dissolved, and the resulting mixed solution was used as a dispersion medium; 160g of barium sulfate with an average particle diameter of 2 μm was added to a sand mill, and then the dispersed The medium is added and the speed of the sand mill is 3500rpm, and the sand is milled for 180min. The solid content of barium sulfate in the dispersion liquid is 80wt%.
Embodiment 2
[0030] Under nitrogen protection, 14.95g of 1,3-bis(4-aminophenoxy)benzene was added to 120g of N,N'-dimethylacetamide until completely dissolved, then 15.1g of 3 was added in batches under mechanical stirring, 3',4,4'-biphenyltetraacid dianhydride, and react with stirring at a reaction temperature below 30°C for 6 hours to obtain a polyamic acid resin solution.
[0031] After premixing 16.7g of titanium dioxide with an average particle size of 100nm and the above polyamic acid resin solution, first mix it in a high-speed mixer with a rotation speed of 5000rpm for 30min, and then ball mill it in a ball mill with a rotation speed of 600rpm for 180min. The solid content of titanium dioxide in the dispersion was 10 wt%.
Embodiment 3
[0033] 60g epoxy resin prepolymer (Epon 828, Shell) is added in 40g methyl ethyl ketone and carry out stirring and dissolving, the mixed solution that obtains is used as dispersion medium; The silica of 75g average particle diameter 500nm is added in the planetary ball mill earlier, then 50 g of the prepared dispersion medium was added and ball milled for 60 min at a rotation speed of 500 rpm. The solid content of silicon dioxide in the dispersion was 60 wt%.
PUM
Property | Measurement | Unit |
---|---|---|
particle diameter | aaaaa | aaaaa |
particle diameter | aaaaa | aaaaa |
particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap