Method for preparing positive pole lead plaster for lead-acid storage battery
A lead-acid battery and positive electrode paste technology, applied in the direction of lead-acid battery electrodes, battery electrodes, circuits, etc., can solve the problems of positive electrode grid corrosion conductivity, positive active material performance deterioration, positive plate matching, etc.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0012] Prepare raw materials: the weight ratio of positive electrode lead paste raw materials is: lead powder 100, lead dioxide 4, thiophene fiber 0.2, sodium sulfate 0.2, deionized water 7.5, active foam carbon material 6, mass percent concentration of 45% sulfuric acid solution 12 , in which the PbO content in the lead powder is 75%, and the length of the thiophene fiber is 1mm.
[0013] After mixing lead dioxide, thiophene fiber, sodium sulfate and activated carbon foam material, put them into the paste mixing machine together with lead powder, and start stirring for 10 minutes.
[0014] Then evenly add 13% pure water accounting for the weight of the mixture, and continue to stir for 6 minutes.
[0015] After adding water, within 23 minutes, add dilute sulfuric acid evenly according to the ratio in the form of spraying. When adding dilute sulfuric acid, turn on the inlet fan and circulating cooling water of the paste machine, control the temperature at 50-55°C, and finish a...
Embodiment 2
[0017] Prepare raw materials: the weight ratio of positive electrode lead paste raw materials is: lead powder 100, lead dioxide 8, thiophene fiber 0.4, sodium sulfate 0.5, deionized water 9, activated carbon foam material 8, mass percent concentration of 45% sulfuric acid solution 14 , wherein the PbO content in the lead powder is 75%, and the length of the thiophene fiber is 3mm.
[0018] After mixing lead dioxide, thiophene fiber, sodium sulfate and activated carbon foam material, add them into the paste mixing machine together with lead powder, and start stirring for 12 minutes.
[0019] After the stirring is completed, 15% pure water by weight of the mixture is evenly added, and the stirring is continued for 6 minutes.
[0020] After adding water and stirring, within 25 minutes, add dilute sulfuric acid evenly according to the proportion in the form of spraying, while adding dilute sulfuric acid, turn on the inlet fan and circulating cooling water of the paste machine, con...
PUM
Property | Measurement | Unit |
---|---|---|
Length | aaaaa | aaaaa |
Length | aaaaa | aaaaa |
Length | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap