Pure-silver wiredrawing knitted flower welding method

A welding method, pure silver technology, applied in clothing, applications, jewelry, etc., can solve the problems of welding traces, uneven surface of welding parts, etc.

Active Publication Date: 2013-12-11
丹寨县国春银饰有限责任公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] As a cultural phenomenon, silver ornaments have been favored by many ethnic groups in history and have become one of the carriers of multicultural exchanges. The processing of silver ornaments of Miao nationality is all done by hand in family workshops; according to needs, silversmiths first smelt silver Made into flakes, silver bars or silver wires, using techniques such as pressing, cutting, engraving, and hugging to make exquisite patterns, and then welding or weaving them into shapes. Welding traces, the surface of the welding part is not smooth and flat
[0003] As can be seen from the above, the above-mentioned existing sterling silver wire drawing braiding welding method obviously has defects and needs to be improved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] Example 1: Bu Yao, a Miao headdress, is welded by multiple silver flakes and silver wires, the welding process

[0012] Include the following steps:

[0013] (1) Grind the pure silver solder piece or electrode into pure silver powder, put the pure silver powder into the copper plate, add borax and purified water, the mass ratio of pure silver powder and borax is: 10:0.8, heat the copper plate with fire , boil the water in the copper pan, and then heat the water in the copper pan for 5-10 seconds to fully dissolve the borax in the boiling water;

[0014] (2) Put the filigree accessories to be welded into the above-mentioned copper plate liquid and soak for 15-25 seconds before taking it out;

[0015] (3) After welding the filigree fittings to the corresponding positions of the silverware, bake them with a flame at 500°C-700°C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a pure-silver wiredrawing knitted flower welding method, which comprises the following steps of: grinding a pure-silver soldering lug or welding rod into pure-silver powder; putting the pure-silver powder in a copper disc; adding borax and pure water, wherein the mass ratio of the pure-silver powder to the borax is 10:0.8; heating the copper disc with fire; boiling water in the copper disc; after the water in the copper disc is boiled, heating for 5-10 seconds to fully dissolve the borax in the boiling water; putting a filament accessory which needs to be welded in the copper disc liquid to be dipped for 15-25 seconds; taking out the filament accessory after 15-25 seconds; welding the filament accessory on the corresponding position of a silverware; and baking with flame of 500-700DEG C. People can not see the welding mark of a silver jewelry welded with the method, and the appearance of the silver jewelry is smooth and flat.

Description

technical field [0001] The invention relates to a processing method of pure silver, in particular to a pure silver wire drawing braiding welding method. Background technique [0002] As a cultural phenomenon, silver ornaments have been favored by many ethnic groups in history and have become one of the carriers of multicultural exchanges. The processing of silver ornaments of Miao nationality is all done by hand in family workshops; according to needs, silversmiths first smelt silver Made into flakes, silver bars or silver wires, using techniques such as pressing, cutting, engraving, and hugging to make exquisite patterns, and then welding or weaving them into shapes. Welding traces, the surface of the welding part is not smooth and flat. [0003] As can be seen from the above, the above-mentioned existing sterling silver wire drawing braiding welding method obviously has defects and needs to be improved. [0004] Therefore, the present invention realizes that the above-...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A44C27/00
Inventor 王国春
Owner 丹寨县国春银饰有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products