Sizing process of fine denier circular hole bright polyamide multifilament

A technology of round holes and nylon, which is applied in the field of sizing technology of fine-denier round-hole glossy nylon multifilaments, which can solve the problems of low weaving efficiency of multifilament nylon fabrics, reduce the probability of wool yarn generation, reduce the incidence of hairiness, and prevent warp breakage Effect

Inactive Publication Date: 2012-12-19
WUJIANG FUHUA WEAVING
View PDF1 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Aiming at the problems existing in the above-mentioned prior art, the present invention solves the low weaving efficiency of the multifilament nylon fabrics of the fine-denier round-hole glossy nylon multifilament series by adjusting the process parameters of the four processes of warping, sizing, paralleling and weaving. series of questions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A sizing process for fine-denier round-hole glossy nylon multifilaments, comprising four steps of warping, sizing, paralleling, and weaving, characterized in that the process parameters of the four steps are as follows:

[0020] (1) Warping: the number of warping strips is 1600, the vehicle speed is 250rpm, the coiling tension is 10kg, and the pressing roller pressure is 2kg;

[0021] (2) Sizing: unwinding tension is 6kg, coiling tension is 10kg, immersion pressure is 3.2kg / cm 2 , the grouting pressure is 2kg / cm 2 , the elongation is 0.15%, the slurry temperature is 40 °C, the temperature of the two drying rooms is: drying room 1 is 150 °C, drying room 2 is 150 °C; five cylinder temperatures: cylinder 1 is 120 °C, cylinder 2 120°C, 115°C for cylinder 3, 115°C for cylinder 4, and 110°C for cylinder 5; the speed is 200m / min, the mixing concentration is 14 bars (solid content), and the sizing rate is 12%;

[0022] (3) Parallel axis: the vehicle speed is 50m / mim, the unwi...

Embodiment 2

[0025] A sizing process for fine-denier round-hole glossy nylon multifilaments, comprising four steps of warping, sizing, paralleling, and weaving, characterized in that the process parameters of the four steps are as follows:

[0026] (1) Warping: the number of warping strips is 1600, the vehicle speed is 300rpm, the coiling tension is 8kg, and the pressing roller pressure is 3kg;

[0027] (2) Sizing: unwinding tension is 6kg, coiling tension is 10kg, immersion pressure is 2.2kg / cm 2 , the grouting pressure is 2.5kg / cm 2 , the elongation is 0.15%, the slurry temperature is 50 °C, the temperature of the two drying rooms is: drying room 1 is 150 °C, drying room 2 is 150 °C; five cylinder temperatures: cylinder 1 is 120 °C, cylinder 2 120°C, 115°C for cylinder 3, 115°C for cylinder 4, and 110°C for cylinder 5; the speed is 200m / min, the mixing concentration is 14 bars (solid content), and the sizing rate is 12%;

[0028] (3) Parallel shaft: the vehicle speed is 50m / mim, the un...

Embodiment 3

[0031] A sizing process for fine-denier round-hole glossy nylon multifilaments, comprising four steps of warping, sizing, paralleling, and weaving, characterized in that the process parameters of the four steps are as follows:

[0032] (1) Warping: the number of warping strips is 1600, the vehicle speed is 350rpm, the coiling tension is 6kg, and the pressing roller pressure is 4kg;

[0033] (2) Sizing: unwinding tension is 6kg, coiling tension is 10kg, immersion pressure is 1.7kg / cm 2 , the grouting pressure is 3.5kg / cm 2 , the elongation is 0.05%, the slurry temperature is 60 °C, the temperature of the two drying rooms is: drying room 1 is 150 °C, drying room 2 is 150 °C; five cylinder temperatures: cylinder 1 is 120 °C, cylinder 2 120°C, 115°C for cylinder 3, 115°C for cylinder 4, and 110°C for cylinder 5; the speed is 200m / min, the mixing concentration is 14 bars (solid content), and the sizing rate is 12%;

[0034] (3) Parallel shaft: the vehicle speed is 50m / mim, the un...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a sizing process of a fine denier circular hole bright polyamide multifilament. By adjusting the technological parameters of four procedures such as warping, sizing, re-beaming and weaving, a good size film is formed on the surface of the fine denier circular hole polyamide filament and is convenient for weaving, the production efficiency is above 95% and a series of problems such as low weaving efficiency of multifilament woolen fabrics of fine denier circular hole bright polyamide multifilament series are solved.

Description

technical field [0001] The invention relates to the field of textiles, in particular to a sizing process for fine-denier round-hole bright nylon multifilaments. Background technique [0002] Fine denier nylon multifilament is more and more widely used in chemical fiber fabrics, and the requirements for fabric quality are getting higher and higher, especially the demand for fine denier glossy multifilament fabrics with round holes is more eager. As we all know, the quality of fine-denier glossy nylon multifilament fabrics with round holes is better, and the raw materials must be better first, but this is far from enough; if the production process cannot be smoothly produced, the weaving efficiency will not reach 95%, and the production cost is high, which cannot meet the modernization of enterprises. production needs. Fine-denier round-hole "●" nylon yarns are less likely to form a good size film than special-shaped cross-section "▲" nylon yarns. Without good size film forma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06B3/04D06B15/00D02H5/02
Inventor 肖燕秦峰李海燕季青
Owner WUJIANG FUHUA WEAVING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap