Modified nano mineral powder-containing aerated brick

A technology of mineral powder and aerated bricks, applied in the field of aerated bricks, can solve the problems of low strength of aerated bricks, and achieve the effects of protecting the environment, reducing energy consumption and reducing bulk density

Active Publication Date: 2013-01-16
广东合盛建筑工程有限公司
View PDF2 Cites 40 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

, but generally the strength of air-entrained brick

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] An aerated brick containing modified nano-mineral powder, which is made from the following weight (kg) raw materials according to the conventional manufacturing process of aerated bricks: 25 carbide slag, 5 cement, 10 quicklime, 5 modified nano-mineral powder , shell powder 2, volcanic rock powder 1, gypsum 3, aluminum powder 0.1, sodium lauryl sulfate 0.008, tea seed cake powder 0.08, soda ash 0.3, expanded vermiculite powder 0.5, zinc stearate 0.3, aluminum hydroxide 0.013, double Sodium acetate 0.1, appropriate amount of water;

[0023] The preparation method of modified nano-mineral powder is as follows: mix 8kg calcium carbonate, 1kg iron ore tailings, 1kg shale, 4kg phosphorus slag, and 3kg sepiolite powder, burn them at 700°C for 5 hours, and grind them into nano Powder, mixed with 2% epoxy octyl stearate and 2% calcium lignosulfonate equivalent to the weight of the powder, stirred evenly, dried, and crushed into powder to get the product;

[0024] The preparati...

Embodiment 2

[0028] An aerated brick containing modified nano-mineral powder, which is made from the following weight (kg) raw materials according to the conventional manufacturing process of aerated bricks: 25 carbide slag, 10 cement, 15 quicklime, 5 modified nano-mineral powder , shell powder 2, volcanic rock powder 1, gypsum 3, aluminum powder 0.1, sodium lauryl sulfate 0.002, tea seed cake powder 0.03, soda ash 0.5, expanded vermiculite powder 0.8, zinc stearate 0.3, aluminum hydroxide 0.01, double Sodium acetate 0.05, appropriate amount of water;

[0029] The preparation method of modified nano-mineral powder is as follows: 9kg calcium carbonate, 1.5kg iron ore tailings, 2kg shale, 2.5kg phosphate rock slag, 3kg sepiolite powder are mixed and burnt at 600°C for 4 hours, and then ground into nano-powder, mixed with 1% epoxy octyl stearate and 1% calcium lignosulfonate equivalent to the weight of the powder, stirred evenly, dried, and pulverized into powder.

[0030] The preparation me...

Embodiment 3

[0037] An aerated brick containing modified nano-mineral powder, which is made from the following weight (kg) raw materials according to the conventional manufacturing process of aerated bricks: 25 carbide slag with a fineness of 200 mesh, 10 cement, 15 quicklime, modified Non-toxic nano mineral powder 5, shell powder with a fineness of 100 mesh 2, volcanic rock powder with a fineness of 180 mesh 1, gypsum 3, aluminum powder 0.1, sodium lauryl sulfate 0.002, tea seed cake powder 0.03, soda ash 0.5, fineness 0.8 for 180-mesh expanded vermiculite powder, 0.3 for zinc stearate, 0.01 for aluminum hydroxide, 0.05 for sodium diacetate, and an appropriate amount of water;

[0038] The preparation method of modified nano-mineral powder is as follows: mix 8kg calcium carbonate, 1kg iron ore tailings, 2kg shale, 2.5kg phosphate rock slag, and 3kg sepiolite powder, burn them at 700°C for 4 hours, and grind them into Nano powder, mixed with 1% epoxy octyl stearate and 1% calcium lignosulf...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Average densityaaaaaaaaaa
Compressive strengthaaaaaaaaaa
Average densityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a modified nano mineral powder-containing aerated brick. The aerated brick is prepared from the following raw materials by the conventional process for preparing the aerated brick: 25 to 30 weight parts of carbide slag, 5 to 10 weight pars of cement, 10 to 15 weight parts of quick lime, 5 to 10 weight parts of modified nano mineral powder, 5 to 10 weight parts of shell powder, 3 to 5 weight parts of gypsum, 0.05 to 0.1 weight part of aluminum powder, 0.002 to 0.008 weight part of lauryl sodium sulfate, 0.03 to 0.08 weight part of tea seed cake powder, 0.3 to 0.5 weight part of soda ash, 0.5 to 0.8 weight part of expanded vermiculite powder, 0.3 to 0.5 weight part of zinc stearate, 0.01 to 0.03 weight part of aluminum hydroxide, 0.05 to 0.1 weight part of sodium diacetate and an appropriate amount of water. By adding the nano mineral powder, the volume weight of the brick, and the energy consumption are reduced; the brick is high in thermal insulation performance and sound insulation performance; compared with the conventional aerated brick, the aerated brick has the advantages that the thermal insulation performance and the sound insulation performance are improved obviously; the raw materials are mixed according to an optimized formula; and the intensity and the freezing resistance of the brick are improved obviously.

Description

Technical field [0001] The present invention involves the field of brick, which is precisely a gas -added brick containing modified nano -mineral powder. Background technique [0002] Aerated concrete is a new type of wall building material. It is unique that it is a very light new building wall material with a very light insulation and insulation.Qi concrete technology began one hundred years ago, and this technology in my country began to be relatively late, 40 years behind abroad. However, the development of the gas -added concrete industry in my country is indeed very fast.At present, the level of gas -added concrete technology technology can already reach the international advanced level. [0003] The biggest advantage of gas -added concrete is to save land resources without waste a lot of cultivated land, and its sources of raw materials are very extensive. Gray sand, slag, stabs, and coal gangsters are all raw materials for gas -added concrete.In addition, the performance ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/00C04B38/02
Inventor 晋元龙陈德全
Owner 广东合盛建筑工程有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap