Solar energy electrical conduction slurry and preparation method thereof
A technology of conductive paste and solar energy, applied in the direction of conductive materials dispersed in non-conductive inorganic materials, cable/conductor manufacturing, circuits, etc., can solve problems such as silicon wafer bending, achieve low warpage, and high photoelectric conversion efficiency , good warpage effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0017] Example 1
[0018] (1) Prepare an organic adhesive. According to the above organic adhesive formula, weigh 12 parts by weight of ethyl cellulose, 1 part of turpentine, 20 parts of dibutyl phthalate, and 10 parts of acrylic resin. Dissolve at 80°C to obtain an organic adhesive;
[0019] (2) Prepare the glass binder, according to the above glass binder formula, weigh out parts by weight of each oxide powder, 10 parts by weight of silicon dioxide, 5 parts of alumina, 1 part of bismuth oxide, 2 parts of zinc oxide, and oxide Calcium 10 parts, mixed uniformly, put into crucible, put into high temperature resistance furnace, heat up to 1050℃, smelt for 50min, quench the melted glass and put it into ball mill jar, ball mill for 30 hours, obtain glass binder , Dry for standby;
[0020] (3) Prepare conductive paste, take 75 parts of aluminum powder, 9 parts of organic binder, 5 parts of glass binder, 1.5 parts of silane coupling agent, and 0.5 parts of dispersant according to the wei...
Example Embodiment
[0021] Example 2
[0022] (1) Prepare an organic adhesive. According to the above organic adhesive formula, weigh 25 parts by weight of ethyl cellulose, 4 parts of turpentine, 30 parts of dibutyl phthalate, and 15 parts of acrylic resin. Dissolve at 60°C to obtain an organic adhesive;
[0023] (2) Prepare the glass binder. According to the formula of the glass binder, weigh each oxide powder, 30 parts by weight of silica, 2 parts of alumina, 0.05 parts of bismuth oxide, 4 parts of zinc oxide, and oxide Calcium 20 parts, mixed uniformly, put into crucible, put into high temperature resistance furnace, heat up to 1200℃, smelt for 35min, quench the melted glass and put it into the ball mill tank and ball mill. After ball milling for 30 hours, the glass binder is obtained , Dry for standby;
[0024] (3) Prepare conductive paste, take 80 parts of aluminum powder, 25 parts of organic binder, 8 parts of glass binder, 0.02 parts of silane coupling agent, and 1 part of dispersant according ...
Example Embodiment
[0025] Example 3
[0026] (1) Prepare an organic adhesive. According to the above organic adhesive formula, weigh 20 parts by weight of ethyl cellulose, 3 parts of turpentine, 25 parts of dibutyl phthalate, and 5 parts of acrylic resin. Dissolve at 70°C to obtain an organic adhesive;
[0027] (2) Prepare a glass binder. According to the above glass binder formula, weigh out parts by weight of each oxide powder, 20 parts of silica, 10 parts of alumina, 3 parts of bismuth oxide, 2 parts of zinc oxide, and oxidation Calcium 15 parts, mixed uniformly, put into crucible, put into high temperature resistance furnace, heat up to 1080 ℃, smelt for 60 minutes, quench the melted glass and put it into ball mill tank and ball mill. After ball milling for 30 hours, a glass binder is obtained , Dry for standby;
[0028] (3) Prepare conductive paste, take 72 parts of aluminum powder, 15 parts of organic binder, 6 parts of glass binder, 3 parts of silane coupling agent, and 2 parts of dispersant a...
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Granularity | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap