Preparation method of Y4Si3O12 whisker toughened Y2SiO5 composite coating

A composite coating and whisker technology, applied in the field of C/C composite materials, can solve the problems of unreachable, easy to fall off, oxidation protection time, etc.

Active Publication Date: 2014-03-12
吴文婕
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the above-mentioned coatings still cannot meet the practical application requirements under the condition of 1600-2500°C high-speed ion flow erosion, and the high-temperature oxidation-resistant ceramic coating of carbon / carbon composite materials is easy to fall off and the oxidation protection time is short in the high-speed gas erosion environment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of Y4Si3O12 whisker toughened Y2SiO5 composite coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Step 1: C / C composite material pretreatment:

[0030] 1) Take the 2D-C / C composite material used for aircraft brake pads and process it into 35×35×35mm 3 The cube, and the surface treatment of grinding and chamfering, the chamfering is 30°;

[0031] 2) Then use deionized water and absolute ethanol to ultrasonically clean 4 times respectively, the ultrasonic time for each cleaning is 10min, the ultrasonic power is 80W, and finally dry in an electric blast drying oven at 50°C.

[0032] Step 2: Prepare SiC porous inner coating on the surface of C / C composite substrate by embedding method

[0033] 1) First, take commercially available analytically pure Si powder, C powder and B powder with a particle size of 20-30 μm 2 o 3 Powder, according to Si powder: C powder: B 2 o 3 Powder = 3:5:0.5 mass ratio to prepare embedding powder, then put the pretreated C / C composite material into a graphite crucible, and embed it in the embedding powder;

[0034] 2) Next, put the graph...

Embodiment 2

[0047] Step 1: C / C composite material pretreatment:

[0048]1) Take the 2D-C / C composite material used for aircraft brake pads and process it into 38×38×38mm 3 The cube, and its surface treatment of grinding and chamfering, the chamfering is 35°;

[0049] 2) Then use deionized water and absolute ethanol to ultrasonically clean 3 times respectively, the ultrasonic time for each cleaning is 20min, and the ultrasonic power is 100W, and finally dry in an electric blast drying oven at 55°C.

[0050] Step 2: Prepare SiC porous inner coating on the surface of C / C composite substrate by embedding method

[0051] 1) First, take commercially available analytically pure Si powder, C powder and B powder with a particle size of 20-30 μm 2 o 3 Powder, according to Si powder: C powder: B 2 o 3 Powder = 4:4:0.8 mass ratio to prepare embedding powder, then put the pretreated C / C composite material into a graphite crucible, and embed it in the embedding powder;

[0052] 2) Next, put the g...

Embodiment 3

[0064] Step 1: C / C composite material pretreatment:

[0065] 1) Take the 2D-C / C composite material used for aircraft brake pads and process it into 40×40×40mm 3 The cube, and its surface treatment of grinding and chamfering, the chamfering is 40°;

[0066] 2) Then use deionized water and absolute ethanol to ultrasonically clean 5 times respectively, the ultrasonic time of each cleaning is 30min, the ultrasonic power is 120W, and finally dry in an electric blast drying oven at 60°C.

[0067] Step 2: Prepare SiC porous inner coating on the surface of C / C composite substrate by embedding method

[0068] 1) First, take commercially available analytically pure Si powder, C powder and B powder with a particle size of 20-30 μm 2 o 3 Powder, according to Si powder: C powder: B 2 o 3 Powder = 5:6:1.0 mass ratio to prepare embedding powder, then put the pretreated C / C composite material into a graphite crucible, and embed it in the embedding powder;

[0069] 2) Next, put the graph...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
melting pointaaaaaaaaaa
melting pointaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of an Y4Si3O12 whisker toughened Y2SiO5 composite coating. The preparation method comprises the following steps of: preparing a SiC porous internal coating on the surface of a C / C composite material substrate by using an embedding method; preparing Y4Si3O12 whisker and performing surface modification on the Y4Si3O12 whisker by using composite surfactant to obtain mixed solution; performing ultrasonic electrophoresis selective assembly and deposition by using the C / C composite material prepared with the SiC porous internal coating on the surface and the mixed solution to obtain a Y4Si3O12 whisker pinning layer; and finally preparing the Y4Si3O12 whisker toughened Y2SiO5 composite coating by using a hydrothermal electrophoretic deposition method. According to the Y4Si3O12 whisker toughened Y2SiO5 composite coating, the time for stable work of the Y4Si3O12 whisker toughened Y2SiO5 composite coating in a high-temperature gas erosion atmosphere is effectively prolonged; and according to the preparation process, the compactness of the coating, the cohesion of a nanocoating and the binding force of internal and external coatings are greatly improved, and subsequent treatment is avoided.

Description

technical field [0001] The invention belongs to the technical field of C / C composite materials, and relates to a method for preparing a high-temperature anti-oxidation coating of C / C composite materials, in particular to a Y 4 Si 3 o 12 Whisker Toughened Y 2 SiO 5 Preparation method of composite coating. Background technique [0002] Carbon / carbon (C / C) composites have excellent properties such as low thermal expansion coefficient, low density, high temperature resistance, ablation resistance, high strength, high modulus, etc. The excellent performance that the amount increases with the increase of temperature makes it have broad application prospects in the aerospace field. However, C / C composites will be oxidized in an aerobic environment exceeding 450 °C, and the loss of oxidized mass will lead to a decrease in its strength, which limits its practical application. Therefore, solving the problem of high-temperature oxidation resistance of C / C composites is the key to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/81C04B41/89
Inventor 黄剑锋杨柳青曹丽云王雅琴费杰
Owner 吴文婕
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap