Production process of fireproofing anti-flaming adhesion agent for exterior wall external insulation phenolic foam board
A technology of phenolic foam board and external wall insulation, which is applied in the direction of fireproof coatings, alkali metal silicate coatings, etc., can solve the problems of plastering materials falling off, poor use of fireproof and flame retardant interface agents, etc., to prevent pulverization and Effects of slag dropping, solving the problem of high temperature resistance, and increasing packing density
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0018] Example 1
[0019] A kind of production process of the fire-proof and flame-retardant interface agent used for external wall insulation phenolic foam board is: select the water glass of modulus 3.1-3.4, triethanolamine, ammonium polyphosphate, pentaerythritol, emulsifier OP-10, water is Raw materials are prepared according to the following weight percentages:
[0020] water glass 12;
[0021] Triethanolamine 12;
[0022] Ammonium polyphosphate 35;
[0023] Pentaerythritol 15;
[0024] Emulsifier OP-10 1;
[0025] water 25;
[0026] The production process is as follows: firstly add water and emulsifier OP-10 into the reaction kettle, start the mixer, and stir for 8 minutes, then add ammonium polyphosphate and pentaerythritol into the reaction kettle in turn, adjust the speed of the mixer to 320 rpm, Control the reaction temperature at 80°C and stir for 1.5 hours; then adjust the speed of the mixer to 280 rpm, then add water glass and triethanolamine to the reactor ...
Example Embodiment
[0027] Example 2
[0028] A kind of production process of the fire-proof and flame-retardant interface agent used for external wall insulation phenolic foam board is: select the water glass of modulus 3.1-3.4, triethanolamine, ammonium polyphosphate, pentaerythritol, emulsifier OP-10, water is Raw materials are prepared according to the following weight percentages:
[0029] water glass 10;
[0030] Triethanolamine 15;
[0031] Ammonium polyphosphate 28;
[0032] Pentaerythritol 16;
[0033] Emulsifier OP-10 1;
[0034] water 30;
[0035] The production process is as follows: firstly add water and emulsifier OP-10 into the reaction kettle, start the mixer, and stir for 6 minutes, then add ammonium polyphosphate and pentaerythritol into the reaction kettle in turn, adjust the speed of the mixer to 350 rpm, Control the reaction temperature at 85°C and stir for 1.5 hours; then adjust the speed of the mixer to 250 rpm, then add water glass and triethanolamine to the reactor ...
Example Embodiment
[0036] Example 3
[0037] A kind of production process of the fire-proof and flame-retardant interface agent used for external wall insulation phenolic foam board is: select the water glass of modulus 3.1-3.4, triethanolamine, ammonium polyphosphate, pentaerythritol, emulsifier OP-10, water is Raw materials are prepared according to the following weight percentages:
[0038] water glass 14;
[0039] Triethanolamine 10;
[0040] Ammonium polyphosphate 28;
[0041] Pentaerythritol 20;
[0042] Emulsifier OP-10 2;
[0043] water 26;
[0044] The production process is: firstly add water and emulsifier OP-10 into the reaction kettle, start the mixer, and stir for 10 minutes, then add ammonium polyphosphate and pentaerythritol into the reaction kettle in turn, adjust the speed of the mixer to 400 rpm, Control the reaction temperature at 90°C and stir for 1.5 hours; then adjust the speed of the mixer to 260 rpm, then add water glass and triethanolamine to the reactor for stirri...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap