Nano attapulgite modified composite sound absorbing material and preparation method thereof

A nano-attapulgite and nano-attapulgite technology are applied in the field of nano-attapulgite-modified composite sound-absorbing materials and their preparation fields to achieve the effects of high breaking strength, high tensile strength and high elongation

Active Publication Date: 2013-03-20
芜湖跃飞新型吸音材料股份有限公司
View PDF3 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Used for spinning to make sound-absorbing cotton

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] A composite sound-absorbing material modified by nano-attapulgite, which is made of the following raw materials in parts by weight: 108 parts of barite powder, 55 parts of ceramsite, 48 parts of nano-attapulgite, 85 parts of styrene-acrylic emulsion, modified tree ash 58 parts, 16 parts of zinc borate, 22 parts of mineral wool fiber, 15 parts of nano carbon, 25 parts of EVA, 18 parts of POE, 8 parts of EMDP, 6 parts of trioctyl trimellitate, 5 parts of triphenyl phosphate, stearin Zinc acid 2 parts, dibasic lead phosphite 1.5 parts.

[0016] Wherein, the modified tree ashes are prepared by the following method: first soak the tree ashes with 10% hydrochloric acid for 4 hours, wash them with deionized water, then soak them with 12% sodium hydroxide solution for 3 hours, and then wash them with deionized water until medium properties, drying, adding 2.5% sodium lignosulfonate, 1.5% methyltriethoxysilane, 2% epoxidized triglyceride, 4% ceramic powder equivalent to the weig...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

The invention discloses a nano attapulgite modified composite sound absorbing material. The material is prepared from the following raw materials in parts by weight: 100-120 parts of barite powder, 50-60 parts of ceramsite, 40-50 parts of nano attapulgite, 80-90 parts of styrene-acrylic emulsion, 55-65 parts of modified tree ashes, 15-20 parts of zinc borate, 20-30 parts of mineral wool fibers, 10-20 parts of nanocarbon, 20-30 parts of EVA (ethylene-vinyl acetate copolymer), 15-20 parts of POE (polyolefin elastomer), 5-10 parts of EMDP, 5-8 parts of trioctyl trimellitate, 4-6 parts of triphenyl phosphate, 2-3 parts of zinc stearate and 1-2 parts of dibasic lead phosphite. The material has the beneficial effects that the problem of developing and researching the sound absorbing material urgently is solved and the novel sound absorbing material which meets the requirements, can stand the tests of harsh environments and has the advantages of high tensile strength, high elongation, high breaking strength, good sound absorbing effect and the like is prepared.

Description

technical field [0001] The invention relates to a nano-attapulgite-modified composite sound-absorbing material and a preparation method thereof, belonging to the technical field of material research and production. [0002] Background technique [0003] With the development of industrial production, transportation, and urban construction, as well as the increase of population density and the increase of household facilities (audio, air conditioning, television, etc.), environmental noise is becoming more and more serious, and it has become a major public hazard that pollutes the human social environment. Noise not only affects hearing, but also has adverse effects on the human cardiovascular system, nervous system, and endocrine system. [0004] Existing sound-absorbing materials also have composite types, but few have excellent performance indicators for composites of inorganic materials and organic materials. On the whole, my country's sound-absorbing material industry ha...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L25/14C08L23/08C08K13/06C08K3/34C08K3/38C08K3/04C08K5/12C08K5/098C08K5/523
Inventor 王黎明孙益民章云厉曼
Owner 芜湖跃飞新型吸音材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com