Modified investment casting shell manufacturing method

An investment casting and module technology, which is applied to casting molding equipment, casting molds, and casting mold components, etc., can solve the problems of poor quality of casting blanks, high surface roughness of castings, increase production costs, etc., and improve the quality of mold shells. , The effect of improving the quality of castings and reducing production costs

Inactive Publication Date: 2013-04-24
QINGDAO SANHESHAN CASTING GROUP
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Nowadays, the development of science and technology is changing with each passing day, and the level of casting technology is also developing rapidly. For investment casting, the existing water glass plus silica sand process has high surface roughness and poor quality of casting blanks. In order to solve this problem, the research and development The advanced silica sol plus zirconium sand process, although the quality of the blank has been improved, it has also greatly increased the production cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0022] An improved method of investment casting shell making of this embodiment includes the following steps:

[0023] (1) Cleaning: remove the oil stains on the surface of the module;

[0024] (2) Paint: After mixing the paint evenly, cover the surface of the module evenly;

[0025] (3) Sanding: Sprinkle a layer of sand evenly on the surface of the coating module

[0026] (4) Hardening: Put the sanded module into the hardening liquid to soak and harden;

[0027] (5) Air-drying: After the module is hardened in the pool, it is proposed to hang on the shelf for water-controlled air-drying;

[0028] (6) Dewaxing: After air drying, put the module in pre-heated water at a temperature of 90℃ to melt the wax mold in the shell;

[0029] In the above steps, the coating, sanding, hardening, and air-drying are repeated 8 times. For the first and second sanding, zircon sand with a particle size group of 15 is used as surface sand, and the third and fourth sanding uses silica sand with a particle size...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a modified investment casting shell manufacturing method. A shell is obtained through steps of cleaning the surface of a mold set, coating, stuccoing, hardening and air drying, wherein the steps of coating, stuccoing, hardening and air drying are repeated 8 times, zircon sand with the granularity group of 15 is used as surface layer sand in the first stuccoing and the second stuccoing, silica sand with the granularity group of 30 is used in the third stuccoing and the fourth stuccoing, silica sand with the granularity group of 60 is used from the fifth stuccoing to the eighth stuccoing, and a water dissolving method using water at 90DEG C is adopted for dewaxing. According to the modified investment casting shell manufacturing method, the zircon sand with the granularity group of 15 is used as the surface layer sand, the thermal expansion coefficient of the zircon sand is low and uniform, and the zircon sand is difficult to chemically react with iron oxide and accordingly has a good sand burning resisting function, quality of the shell is improved, and the zircon sand is high in price, the silica sand is used from the third stuccoing to the eighth stuccoing, so that production cost is reduced on the premise of obtaining a high quality casting.

Description

[0001] Technical field [0002] The invention belongs to the field of casting technology, and specifically relates to a method for making a shell by investment casting. [0003] Background technique [0004] The investment casting production process mainly includes three processes: mold making, shell making, and shell roasting and pouring. The shell making process is the wax module made by the mold making process through multiple cycles of coating, sanding, hardening, and air drying. The coating module is formed in the process, and then dewaxing (melting the wax mold) is performed to form the mold shell, and the cavity in the shell is the part model. [0005] With the rapid development of science and technology, the level of casting technology is also developing rapidly. For investment casting, the existing water glass and silica sand technology has high surface roughness and poor quality of castings. To solve this problem, the research and development Although the quality of the bl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22C9/04B22C7/02
Inventor 李宁波
Owner QINGDAO SANHESHAN CASTING GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products