Glass fiber soakage agent for producing transparent sheet yarns

A glass fiber and transparent plate technology, applied in the field of glass fiber sizing, can solve the problems of dispersibility, soaking speed, antistatic performance and transparency, fiber bundle and chopping performance can not meet the processing requirements, film forming agent and Solve problems such as large differences in the refractive index of the matrix resin, to achieve the effect of ensuring strength, good stiffness, and reducing hairiness

Active Publication Date: 2015-06-03
NEIJIANG HUAYUAN ELECTRONICS MATERIALS
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, domestic sizing agents for transparent boards generally use unsaturated polyester or PVAC emulsion alone. If unsaturated polyester emulsion is used alone, the fiber bundling and chopping properties cannot meet the processing requirements; if PVAC emulsion is used alone, the dispersibility and penetration speed The conflict cannot be resolved; at the same time, the refractive index difference between the film-forming agent and the matrix resin is large, which cannot meet the high transparency requirements
Existing sizing agents for transparent boards cannot solve the problems of dispersibility, penetration speed, antistatic performance and transparency at the same time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] The glass fiber sizing used to produce transparent sheet yarn is made of the following raw materials in weight ratio:

[0021] Vinyltriethoxysilane 0.10%

[0022] Epoxy modified polyester resin emulsion 2.5%

[0023] Polyethylene glycol nonionic surfactant 0.04%

[0024] Lithium chloride 0.50%

[0025] Glacial acetic acid 0.08%

[0026] The balance is deionized water.

[0027] The sizing agent of the present invention is applied to the production of transparent sheet yarns. The generally used wire drawing process is 1600-hole platinum bushing wire drawing. The final raw wire is formed by plying 80 yarn bundles, and the diameter of the single fiber is controlled at 12 microns. The process can be dried by steam and hot air, the drying time is 13.5 hours, the final product is 2400Tex, and the LOT% is 0.5±0.15%.

[0028] The performance test of glass fiber produced with the above sizing formulation is as follows:

[0029] Hairiness 0.65mg / kg; Stiffness 115mm; Electros...

Embodiment 2

[0031] The glass fiber sizing used to produce transparent sheet yarn is made of the following raw materials in weight ratio:

[0032] Vinyltriethoxysilane 0.30%

[0033] Epoxy modified polyester resin emulsion 5.0%

[0034] Polyethylene glycol nonionic surfactant 0.04%

[0035] Lithium chloride 0.50%

[0036] Glacial acetic acid 0.08%

[0037] The balance is deionized water.

[0038] The sizing agent described in the present invention is applied to the production of transparent board yarns. The generally used wire drawing process is 1600-hole platinum bushing wire drawing, and each final raw wire is formed by plying 80 yarn bundles, and the single fiber diameter is controlled at 12 microns. The drying process can use steam and hot air drying, the drying time is 13.5 hours, the final product is 2400Tex, and the LOT% is 0.5±0.15%.

[0039] The performance test of glass fiber produced with the above sizing formulation is as follows:

[0040] Hairiness 1.5mg / kg; Stiffness ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
strengthaaaaaaaaaa
strengthaaaaaaaaaa
dispersityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a glass fiber soakage agent for producing transparent sheet yarns. The glass fiber soakage agent is prepared from 0.10 percent of silane coupling agent, namely vinyl triethoxy silane, 2.5 percent of film former, namely epoxy modified polyester resin emulsion, 0.04 percent of lubricant, namely polyethylene glycol non-ionic surfactant, 0.50 percent of antistatic agent, namely lithium chloride, 0.08 percent of pH regulator, namely glacial acetic acid and water. The transparent sheet yarns produced by the glass fiber soakage agent have the advantages of good dispersibility, high permeation speed, good short cut performance, no-static accumulation, good combination performance with matrix resin, ageing resistance, high light transmittance and stable quality, and the effective use ratio is greatly increased.

Description

technical field [0001] The invention relates to a glass fiber sizing for producing transparent board yarn. Background technique [0002] Fiberglass lighting panels are commonly known as glass fiber reinforced plastics, also known as transparent tiles. It is a lighting material used in conjunction with steel structures. It is mainly composed of high-performance film, reinforced polyester and glass fiber. The film plays a very good role in anti-ultraviolet and anti-static. The anti-ultraviolet is to protect FRP lighting. The polyester of the board does not yellow and age, and loses light transmission properties prematurely. Antistatic is to ensure that the dust on the surface is easily washed away by rain or blown away by the wind, so as to maintain a clean and beautiful surface. Due to its stable quality and durable features, it is widely used in roofs and walls of industrial, commercial and civil buildings. [0003] Glass fiber sizing is the key technology in FRP lighting...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C25/40
Inventor 刘钢刘术明何文倪海威胡校成甘秀丽刘金平
Owner NEIJIANG HUAYUAN ELECTRONICS MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com