Production method of melt direct spinning high-modulus low-shrinkage polyester industrial filament
A high-modulus, low-shrinkage, melt-direct spinning technology, applied in the field of chemical fiber product manufacturing, can solve the problems of high energy consumption and waste yarn rate, and achieve the effects of stable product quality, high production efficiency and easy exchange
Active Publication Date: 2013-05-08
ZHEJIANG GUXIANDAO POLYESTER DOPE DYED YARN CO LTD
View PDF4 Cites 15 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
At present, the production of high-modulus low-shrinkage polyester industrial yarn is mostly slicing method with 3 heads / position and 4 heads / position. The spinning speed is about 5000 m / min, and the energy consumption and waste yarn rate are relatively high.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
Embodiment 2
Embodiment 3
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Property | Measurement | Unit |
---|---|---|
diameter | aaaaa | aaaaa |
height | aaaaa | aaaaa |
diameter | aaaaa | aaaaa |
Login to View More
Abstract
The invention discloses a production method of a melt direct spinning high-modulus low-shrinkage polyester industrial filament, and belongs to the technical field of polyester industrial yarns. The production method is used for a tyre cord. The method comprises melt liquid tackifying, melt direct spinning, draft heat shaping and winding molding. A spinning machine is four heads / position and six heads / position, due to the fact that melt direct spinning is achieved, and limit of the flow of spinning by a spinning screw does not exist. High-modulus low-shrinkage polyester industrial filaments produced according to the technical scheme of the production method are stable in product quality and high in production efficiency, improve the yield of unit time, and lower production energy consumption and production cost. Products can be used as good materials such as tyre cords, geogrids and polyester cords.
Description
technical field [0001] The invention relates to the technical field of chemical fiber product manufacturing, in particular to a production method of melt direct spinning high-modulus low-shrinkage polyester industrial filaments. Background technique [0002] High-modulus low-shrinkage polyester industrial filament, referred to as high-modulus low-shrinkage polyester industrial filament, is an industrial filament with high initial modulus and low thermal shrinkage rate. It has better mechanical properties and high crystallinity. The structure with high degree of orientation, high degree of orientation and high regularity and low internal residual stress are mainly used in rubber skeleton materials, such as automobile cord fabrics and wire ropes. At present, the production of high-modulus low-shrinkage polyester industrial yarn is mostly slicing method with 3 heads / position and 4 heads / position. The spinning speed is about 5000 m / min, and the energy consumption and waste yarn ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01D13/00D01D1/04D01D5/098D01D5/092D01D10/02D01D7/00
Inventor 施建强刘雄高琳金革胡智暄杨志超刘宗杰石教学
Owner ZHEJIANG GUXIANDAO POLYESTER DOPE DYED YARN CO LTD
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Patsnap Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com