185-DEG C lead-free low-temperature alloy for fuse burned-out core and preparation method thereof

A low-temperature alloy and fuse technology, applied in the field of alloys, can solve problems such as harm to human health and environmental pollution, and achieve the effects of low cost, uniform composition, good social and economic benefits

Active Publication Date: 2015-01-07
TIANJIN BAIRUIJIE WELDING MATERIAL
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Fusible core is the heart of the thermal fuse and the technical core of the thermal fuse production process. The traditional thermal fuse is mostly tin-lead alloy. has a lot of pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0025] The present invention is further described below in conjunction with specific embodiment; It should be emphasized that: for those of ordinary skill in the art, can improve or change according to the above description, and all these improvements and changes should belong to the appended claims of the present invention protected range.

[0026] A lead-free low-temperature alloy for a 185°C fuse fuse core, the specific composition of which is Sn 82.5 Cu 0.5 In 14 Ag 3 , the specific ingredients and weight ratio are as follows:

[0027] Cu: 0.5%;

[0028] Ag: 3%;

[0029] In: 15%;

[0030] Sn: 82.5%.

[0031] You can also use the ratio in the following table, the sum is 100%

[0032] chemical composition%

sn

Cu

In

Ag

100%

81.5-83.5

0.4-0.6

13.5-14.5

2.8-3.2

[0033] A method for preparing a 185°C fuse fuse core lead-free low-temperature alloy, the steps are:

[0034] ⑴Put metal tin into a stainless steel cruc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention relates to a 185-DEG C lead-free low-temperature alloy for a fuse burned-out core and a preparation method thereof. The 185-DEG C lead-free low-temperature alloy comprises the following raw materials in percentage by weight: 0.4%-0.6% of Cu, 2.8%-3.2% of Ag, 13.5%-14.5% of In and the balance being Sn. The preparation method of the 185-DEG C lead-free low-temperature alloy comprises the following preparation steps of: putting metal tin to a stainless steel crucible; heating up the crucible by using an electric furnace; adding metal copper at 280-320 DEG C when the tin is molten; adding metal silver after the metal copper is molten down; adding indium after the metal sliver is molten down; conventionally adding a degassing agent for degassing after the indium is molten down; and removing the slag and casting. The lead-free low-temperature alloy containing Sn, Cu, In and Ag disclosed by the invention is used for manufacturing a burned-out core of a temperature fuse, and the melting point of the lead-free low-temperature alloy is 185 DEG C + / -3 DEG C. The low-temperature alloy is eutectic alloy which has the characteristics of good composition uniformity, narrow melting point range, low cost and the like, and is a lead-free environment-friendly material. Moreover, the 185-DEG C lead-free low-temperature alloy has good social benefits and economic benefits.

Description

technical field [0001] The invention belongs to the field of alloys, and relates to a lead-free low-temperature alloy, in particular to a lead-free low-temperature alloy with a fusing core of a 185°C fuse and a preparation method thereof. Background technique [0002] Fusible core is the heart of the thermal fuse and the technical core of the thermal fuse production process. The traditional thermal fuse is mostly tin-lead alloy. There is a lot of pollution. [0003] Low-temperature alloys can be used for the protection of electronic circuits in the electronics industry, and are mostly used to make fuse cores for thermal fuses. At present, the manufacturers of low-temperature alloys leading the world's advanced technology are Alpha in the United States and Senju in Japan. [0004] According to the search, the following patent documents related to this application were found, wherein CN102296208A discloses a lead-free low-temperature alloy for making a fuse core of a thermal...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C13/00H01H85/06H01H69/02
Inventor 黄永利赵世有李洪福付宏宇
Owner TIANJIN BAIRUIJIE WELDING MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com