Novel high-scandium aluminum alloy welding wire
A technology of aluminum alloy welding wire and high scandium, which is applied in welding medium, welding equipment, metal processing equipment and other directions to achieve the effect of improving alloy strength, electrical conductivity and weld strength.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0012] The chemical composition of the new high scandium aluminum alloy welding wire of the present invention is calculated by mass percentage: magnesium Mg: 5.05, manganese Mn: 0.13, titanium Ti: 0.25, zinc Zn: 0.37, chromium Cr: 0.14, zirconium Zr: 0.30, scandium Sc: 1.41, iron Fe: 0.118, silicon Si: 0.147, copper Cu: 0.031, beryllium Be: 0.0003, other single impurity elements ≤ 0.1, other impurity elements total ≤ 0.15, and the balance is aluminum Al. The tensile strength of the high scandium aluminum alloy welding wire in this embodiment is 512 MPa, and the elongation is 17%.
[0013] The aluminum alloy welding wire prepared in this embodiment was used as a filler material, and a 10 mm thick 5083 O state plate was welded by MIG welding at room temperature. Metallographic observation shows that there is a fine equiaxed grain structure in the center of the weld and near the fusion zone, and Al3(Sc, Zr) composite particles are precipitated in the weld during cooling, which ar...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap