High-strength steel plate for 800MPa hydropower station pressure pipeline and production method thereof
A technology for pressure pipelines and high-strength steel plates, which is applied to high-strength steel plates and production fields for 800MPa hydropower station pressure pipelines. Crack susceptibility index, the effect of reducing construction cost and reducing welding difficulty
Active Publication Date: 2013-09-11
SHOUGANG CORPORATION
View PDF14 Cites 31 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
The steel plate composition design and manufacturing process involved in the patent cannot guarantee the performance of the steel plate after strain, and cannot be appli
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0045] Examples of adjusted steel plates with a thickness specification ≤ 60mm produced according to the production method of the present invention are shown in the following tables.
[0046] Table 1 is the composition of the examples of the present invention, Table 2 is the rolling process of the examples of the present invention, Table 3 is the heat treatment process of the examples, and Table 4 is the mechanical properties of the examples. As can be seen from the table, the manufacturing method of the present invention can produce quenched and tempered steel plates for 800MPa grade hydropower station pressure pipes with performance temperature, yield strength ≥ 690MPa, tensile strength ≥ 780MPa, elongation ≥ 16%, and -40 ℃ impact toughness value single Value ≥ 130J.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more PUM
| Property | Measurement | Unit |
|---|---|---|
| Yield strength | aaaaa | aaaaa |
| Tensile strength | aaaaa | aaaaa |
| Impact toughness | aaaaa | aaaaa |
Login to view more
Abstract
The invention provides a high-strength steel plate for an 800MPa hydropower station pressure pipeline and a production method thereof, and belongs to the technical field of steel for hydropower stations. The steel is composed of the following chemical ingredients in percentage by weight: 0.08-0.10% of C, not larger than 0.25% of Si, 1.2-1.6% Mn, not larger than 0.013% of P, not larger than 0.02% of S, 0.01-0.03% of Nb, not larger than 0.03% of V, 0.01-0.02% of Ti, 0.15-0.50% of Ni, 0.20-0.60% of Cr, 0.05-0.30% of Mo, 0.0010-0.0015% of B and the balance of Fe and inevitable impurities. Since element ingredients are reasonably combined and designed and corresponding rolling and heat treatment techniques are matched, the steel plate has excellent welding adaptability while having excellent strength, plasticity and low-temperature impact toughness, and the welding cold cracking sensitivity index Pcm is not larger than 0.22%.
Description
technical field [0001] The invention belongs to the technical field of steel for hydropower stations, and in particular relates to a high-strength steel plate for pressure pipes of 800MPa hydropower stations and a production method. Background technique [0002] During the construction and development of hydropower stations, with the development of units towards high parameters and large capacity, the diameter of pressure steel pipes in hydropower stations is becoming larger and larger. At present, the steel plates commonly used in hydropower stations are 610MPa grades, and it is necessary to ensure the impact toughness of steel plates at -20°C~-40°C. And has good welding adaptability. As the water head of the newly designed hydropower station continues to increase, the design diameter and pressure of the penstock steel pipe continue to increase. Without increasing the strength grade of the steel pipe, the thickness of the steel plate needs to be increased to meet the design...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more Application Information
Patent Timeline
Login to view more IPC IPC(8): C22C38/58C22C38/54C21D8/02
Inventor 隋鹤龙秦丽晔邹扬赵楠吕延春刘美艳刘印良孟冬立张学峰冯路路白学军刘建明张雪松
Owner SHOUGANG CORPORATION
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Try Eureka
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap