Supercharge Your Innovation With Domain-Expert AI Agents!

High-strength plastic

A high-strength plastic, maleic anhydride technology, applied in the field of plastics, can solve the problem of insufficient strength of ABS, and achieve the effect of excellent strength

Inactive Publication Date: 2013-10-02
宁波康德新材料有限公司
View PDF2 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Although ABS is widely used, due to the characteristics of the molecular structure and performance of ABS itself, ABS is insufficient in strength.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength plastic
  • High-strength plastic
  • High-strength plastic

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] Weigh 600 grams of ABS and dry it at 90°C for 4 hours, then mix with 80 grams of silica, 130 grams of glass fiber, 50 grams of γ-aminopropyltriethoxysilane, methyl methacrylate-butadiene- 50 grams of styrene copolymer and 8 grams of monoglyceride stearate were stirred for 5 minutes at 1100 rpm in a high-speed mixer, and released after being uniform. Put the mixed material into the twin-screw extruder with a length-to-diameter ratio (L / D) of 40. The processing temperature of the twin-screw extruder: the temperature in the first zone is 180°C, the temperature in the second zone is 185°C, and the temperature in the third zone is 180°C. The temperature of the fourth zone is 195°C, the temperature of the fourth zone is 210°C, the temperature of the fifth zone is 215°C, the temperature of the sixth zone is 225°C, the temperature of the seventh zone is 235°C, the temperature of the eighth zone is 240°C, and the speed of the main engine is 320 rpm; Afterwards, the stretcher is ...

Embodiment 2

[0016] A high-strength plastic was prepared in the same manner as in Example 1, except that silica was not used.

Embodiment 3

[0018] A high-strength plastic was prepared in the same manner as in Example 1, except that glass fibers were not used.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a high-strength plastic which comprises the following components in parts by weight: 40-70 parts of ABS (acrylonitrile-butadiene-styrene), 3-8 parts of interfacial coupling agent, 3-10 parts of toughener, 0.5-1.0 part of dispersing and lubricating agent, 5-10 parts of silicon dioxide and 10-15 parts of glass fiber. The high-strength plastic provided by the invention has excellent strength, can be widely used in automobile industry, and is often used for manufacturing daily necessities, such as automobile parts, home appliance industry, architectural decoration industry, crash helmets, motorcycle fenders, heelpieces, snowfield sporting goods, toys, clocks, loudspeaker shells, suitcases, buttons, cosmetic cases and the like, and advertising products of nameplates, ornaments and the like.

Description

technical field [0001] The invention relates to the field of plastics, in particular, the invention relates to a high-strength plastic. Background technique [0002] ABS (acrylonitrile-butadiene-styrene) resin is an important general-purpose synthetic resin. The main body is a blend or terpolymer of acrylonitrile, butadiene and styrene. It is a tough and rigid thermoplastic. plastic. It has a wide range of uses. The automobile industry is often used to manufacture auto parts such as instrument panels, body panels, interior trim panels, steering wheels, sound insulation panels, door locks, bumpers, ventilation pipes, etc. The home appliance industry is often used to manufacture such as refrigerators, TVs, etc. Machines, washing machines, vacuum cleaners, food mixers, telephone casings, etc., are commonly used in the construction and decoration industry to manufacture sanitary ware, swimming pool linings, pipes and pipe fittings, etc., and are also used to manufacture safety ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L55/02C08L33/12C08K3/36C08K7/14C08K5/544C08K5/103
Inventor 王永旺康建训
Owner 宁波康德新材料有限公司
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com