Method for adjusting matching degree of forming parameters of coal ash autoclaved standard brick

A technology of parameter matching and adjustment method, which is applied in the field of matching and adjustment of forming parameters of fly ash autoclaved standard bricks

Active Publication Date: 2014-12-17
太原钢铁(集团)有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to overcome the above-mentioned shortcomings of the existing fly ash autoclaved standard brick forming parameter matching adjustment method, the present invention provides a fly ash autoclaved standard brick forming parameter matching adjustment method with a higher qualified rate of standard brick body forming

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0057] This embodiment is a method for matching and adjusting the forming parameters of the production line of 200 million pieces (fly ash autoclaved standard bricks). (Based on the annual brick machine production rate of 91.2%, the output is 25,000 pieces / hour)

[0058] Ⅰ Raw material preparation and dry raw material ratio before dry raw material ratio

[0059] The following a, b, c are raw material preparations before production

[0060] a The standard requirements for technical indicators of quicklime entering the factory: effective CaO content ≥ 58%, digestion time: 8-12 minutes, digestion temperature: 50-60 degrees.

[0061] b The first stage of quicklime crushing adopts a jaw crusher, the gap between the jaw plates is 6-10mm, and the second stage crusher adopts a ball mill, and the grinding time in the ball mill is 3 minutes.

[0062] c The water content of the furnace bottom coarse slag entering the factory: 20-24%, and the large particles ≥ 5mm are screened out befor...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for adjusting the matching degree of forming parameters of a coal ash autoclaved standard brick. The adjusted parameters comprise the following important parameters including dry raw material ratio, feeding door opening time, material distributing bed moving speed and rocking bar swinging times, wherein I, the dry raw materials comprises the following components in parts by mass: 46 to 50 parts of coal ash, 7 to 9 parts of quick lime, 3.6 to 4.4 parts of dust-removing lime, 20 to 24 parts of gravel and 16 to 20 parts of coarse slag, wherein the granularity of the gravel is less than or equal to 5 mm and 9.4 to 10 percent of water is added into the dry materials; II, the feeding door opening time is controlled to be 0.1 to 0.3 second; III, the rated value of the material distributing bed moving speed is 1.8 to 2.2 m / s and the normal set value is 70 to 80 percent of the rated value; IV, technical parameters of material distribution are controlled, i.e., a rocking bar swings for 5 to 6 times and a mould frame charging depth is 220 mm. By adopting the method for adjusting the matching degree of the forming parameters of the coal ash autoclaved standard brick, the blank formation qualified ratio of manufactured standard bricks is high.

Description

technical field [0001] The invention relates to a method for matching and adjusting forming parameters of fly ash autoclaved standard bricks. Background technique [0002] Fly ash autoclaved standard brick is a new type of energy-saving building material, and it is also a substitute for ordinary clay bricks (ie red bricks). In the production process of fly ash autoclaved standard bricks, processes such as raw material processing and preparation, metering and batching, water mixing, digestion and heat release, hydraulic forming, and steam autoclaving operations are involved. Among them, many kinds of production process technical parameters are adjusted and controlled, including: fly ash loss on ignition, fly ash particle size, moisture content of mixture, quicklime digestion time, effective CaO content out of the warehouse, cloth distribution times and charging depth, forming pre-production pressure etc. Forming parameters play a decisive role in the quality and output of f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B30/00
Inventor 胡荣建
Owner 太原钢铁(集团)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com