Negative electrode diachylon used for high-performance AGM battery and preparing method thereof

A negative electrode paste, high-performance technology, applied in the direction of battery electrodes, circuits, electrical components, etc., can solve the problems of poor charge acceptance performance, poor dynamic charge acceptance performance, prone to sulfation of the negative plate, and difficulty in meeting the requirements of starting and stopping. Achieve the effect of comprehensive performance improvement, excellent charging acceptance performance, and improvement of dynamic acceptance characteristics

Active Publication Date: 2013-12-18
骆驼集团蓄电池研究院有限公司
View PDF9 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when it is applied to a start-stop car, it still exists in a partial charge state for a long time, and the negative plate is extremely prone to sulfation, and the charging acceptance performance, especially the dynamic charging acceptance performance, is poor, and the battery life is terminated due to difficulty in charging. Meeting parking requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Negative electrode diachylon used for high-performance AGM battery and preparing method thereof
  • Negative electrode diachylon used for high-performance AGM battery and preparing method thereof
  • Negative electrode diachylon used for high-performance AGM battery and preparing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Add 100kg of lead powder (containing 75% PbO by mass) into the paste mixing machine. Add 0.1kg medium and high specific surface area carbon black, 0.3kg low specific surface area conductive carbon black, 0.5kg ultrafine barium sulfate, 0.1kg sodium lignosulfonate, 0.5kg humic acid into the water mixing tank, and then add 10kg purification Water, stir and mix at a high speed and then pour into the paste mixing machine. After wet mixing with lead powder, the density is 1.400g / cm. 3 (25°C) sulfuric acid 9kg, control the temperature of the paste at 60°C during the paste mixing process, stir evenly, cool down to 40°C, and get the negative lead paste after the paste is produced.

Embodiment 2

[0035] Add 90kg of lead powder (containing 75% PbO by mass) into the paste mixing machine. Add 1kg medium and high specific surface area carbon black, 0.2kg low specific surface area conductive carbon black, 0.3kg ultrafine barium sulfate, 0.1kg sodium lignosulfonate, 0.1kg humic acid into the water mixing tank, then add 10kg purified water , high-speed stirring and mixing evenly and then pouring into the paste mixing machine, after wet mixing with lead powder, the density of rapid pouring is 1.42g / cm 3 (25°C) sulfuric acid 3kg, control the temperature of the paste at 60°C during the paste mixing process, stir evenly, cool down to 40°C, and get the negative lead paste after the paste is produced.

Embodiment 3

[0037]Add 100kg of lead powder (containing 80% PbO by mass) into the paste mixing machine. Add 0.8kg medium and high specific surface area carbon black, 1kg low specific surface area conductive carbon black, 0.5kg ultrafine barium sulfate, 2kg sodium lignosulfonate, 0.2kg humic acid into the water mixing tank, then add 15kg purified water, After mixing at high speed, it is poured into the paste mixing machine. After wet mixing with lead powder, the density is 1.42g / cm. 3 (25°C) sulfuric acid 7kg, control the temperature of the paste at 50°C during the paste mixing process, stir evenly, cool down to 30°C, and get the negative lead paste after the paste is produced.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Specific surface areaaaaaaaaaaa
Specific surface areaaaaaaaaaaa
Resistivityaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of lead storage batteries and relates to a negative electrode diachylon which is capable of improving dynamic charging acceptance performance of an AGM battery and a preparing method thereof. The negative electrode diachylon is capable of improving the dynamic charging acceptance performance of the AGM battery under the condition that the AGM battery has the advantages of being long in service life and strong in starting capacity, the probability of sulfation of a negative plate when the negative plate is in a partial charge state for a long time is reduced, and then starting and shut-down requirements are met.

Description

technical field [0001] The invention belongs to the technical field of lead storage batteries, and relates to a negative electrode lead paste for high-performance AGM batteries and a preparation method thereof, in particular to a negative electrode lead paste for improving the dynamic charge acceptance characteristics of AGM batteries and a preparation method thereof. Background technique [0002] Energy saving and environmental protection is the development direction of future automobiles. Europe has already legislated to reduce the CO of cars by 2015 2 Emissions are reduced to below 120g / km (higher than the Euro IV standard), which makes all European car manufacturers have to adopt new emission reduction systems and auxiliary power units, and use the micro-hybrid with stop / start (start-stop) system For cars, it is only necessary to make minor improvements to the automotive electrical system, change the generator on the existing car to a starter / generator, add a set of sto...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): H01M4/38H01M4/62
CPCY02E60/10
Inventor 李建华钟锐王天成孟刚戴经明高国兴
Owner 骆驼集团蓄电池研究院有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com