Coating composition capable of regulating surface friction coefficient of inner liner for cigarettes
A technology of inner lining paper and surface friction for cigarettes, applied in paper coating, coating, papermaking, etc., can solve problems affecting scratch resistance and smoothness, low friction coefficient, slipping, etc., and increase scratch resistance , Overcome shrinkage cavity and prevent slippery effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0027] Example 1
[0028] This embodiment relates to a scheme for adjusting the friction coefficient of a water-based varnish coating on the surface of a cigarette lining paper, and the scheme includes the following steps:
[0029] (1) Prepare materials according to the following components and contents (parts by weight):
[0030] Component
[0031] Deionized water
[0032] (2) Mix the hard acrylic resin and 10 parts of deionized water, raise the temperature to 60° C., and stir at a low speed of 400 rpm for 8 minutes to obtain an aqueous acrylate solution.
[0033] (3) Add the hand-feeling resin while stirring, and stir for 8 minutes at a low speed of 400 rpm.
[0034] (4) Mix the ethanol and the remaining deionized water evenly, add them to the reaction kettle while stirring, and stir for 8 minutes at a low speed of 400 rpm.
[0035] (5) Add the auxiliary agent to the reaction kettle, and stir for 15 minutes at a medium speed of 750 rpm. A coating composition that can adjust the...
Example Embodiment
[0036] Example 2
[0037] This embodiment relates to a scheme for adjusting the friction coefficient of a water-based varnish coating on the surface of a cigarette lining paper, and the scheme includes the following steps:
[0038] (1) Prepare materials according to the following components and contents (parts by weight):
[0039] Component
[0040] (2) Mix the hard acrylic resin, soft acrylic resin and 4 parts of deionized water, raise the temperature to 60° C., stir at a low speed of 300 rpm for 10 minutes to obtain an aqueous acrylate solution.
[0041] (3) Add the silicon-containing modified acrylic resin and the hand-feeling resin while stirring, and stir at a low speed of 300 rpm for 10 minutes.
[0042] (4) Mix the ethanol and the remaining deionized water evenly, add them to the reaction kettle while stirring, and stir at low speed 300 rpm for 10 minutes.
[0043] (5) Add the auxiliary agent to the reaction kettle and stir at a medium speed of 700 rpm for 20 minutes. A coatin...
Example Embodiment
[0044] Example 3
[0045] This embodiment relates to a scheme for adjusting the friction coefficient of a water-based varnish coating on the surface of a cigarette lining paper, and the scheme includes the following steps:
[0046] (1) Prepare materials according to the following components and contents (parts by weight):
[0047] Component
[0048] (2) Mix the hard acrylic resin, soft acrylic resin and 8 parts of deionized water, raise the temperature to 60° C., stir at a low speed of 500 rpm for 5 minutes to obtain an aqueous acrylate solution.
[0049] (3) Add the silicon-containing modified acrylic resin and the hand-feeling resin while stirring, and stir at a low speed of 500 rpm for 5 minutes.
[0050] (4) Mix the ethanol and the remaining deionized water evenly, add them to the reaction kettle while stirring, and stir for 5 minutes at a low speed of 500 rpm.
[0051] (5) Add the auxiliary agent to the reaction kettle and stir at a medium speed of 800 rpm for 10 minutes. A coat...
PUM
Property | Measurement | Unit |
---|---|---|
Tg | aaaaa | aaaaa |
Tg | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap