Pure acrylic artificial stone as well as manufacturing method thereof

An acrylic and artificial stone technology, applied in the field of pure acrylic artificial stone and its manufacturing, can solve the problems of reducing appearance, feel, weather resistance, heat resistance, water resistance, etc., and achieve excellent thickening performance, excellent appearance and performance effect

Inactive Publication Date: 2014-02-12
江门市德山复合材料科技有限公司
View PDF2 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Disadvantage 1: Reduce the heat resistance and water resistance of the product; Disadvantage

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Pure acrylic artificial stone as well as manufacturing method thereof
  • Pure acrylic artificial stone as well as manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Preparation of thickener:

[0030] Add 400 parts of polymethyl methacrylate (molecular weight: 100,000) and 12,000 parts of methyl methacrylate into a stirred tank equipped with a heating device and a cooling device, and heat to dissolve to prepare thickener a.

[0031] Preparation of acrylic artificial stone:

[0032] Add 30 parts of methyl methacrylate, 10 parts of isobornyl methacrylate, 15 parts of neopentyl glycol dimethacrylate into the kneader as the acrylic resin monomer mixture, 25 parts of the thickener a prepared above , 320 parts of inorganic filler aluminum hydroxide, 0.8 parts of curing agent TBPB, 0.1 part of curing agent t-butyl peroxide maleic anhydride, knead the above raw materials for 10 minutes to obtain an acrylic molding compound. The molding compound was placed in an oven at 60°C, and it was not sticky even immediately after kneading.

[0033] Then, the molding compound was filled into a 20CM flat mold, and cured for 10 minutes at a male mold t...

Embodiment 2

[0036] Preparation of thickener:

[0037] Add 400 parts of polymethyl methacrylate (molecular weight 300,000) and 12,000 parts of methyl methacrylate into a stirred tank equipped with a heating device and a cooling device, heat and dissolve to make thickener b.

[0038] Preparation of acrylic artificial stone:

[0039] Add 20 parts of methyl methacrylate, 20 parts of isobornyl methacrylate, 30 parts of neopentyl glycol dimethacrylate into the kneader as the acrylic resin monomer mixture, 15 parts of the thickener b prepared above , 320 parts of inorganic filler aluminum hydroxide, 0.9 parts of curing agent TBPB, 0.1 part of curing agent t-butyl peroxide maleic anhydride, knead the above raw materials for 10 minutes to obtain an acrylic molding compound. The molding compound was placed in an oven at 60°C, and it was not sticky even immediately after kneading.

[0040] Then, the molding compound was filled into a 20CM flat mold, and cured for 10 minutes at a male mold temperat...

Embodiment 3

[0043] Preparation of thickener:

[0044] Add 400 parts of polymethyl methacrylate (molecular weight 300,000) and 12,000 parts of methyl methacrylate into a stirred tank equipped with a heating device and a cooling device, heat and dissolve to make thickener b.

[0045] Preparation of acrylic artificial stone:

[0046] Add 20 parts of methyl methacrylate, 20 parts of isobornyl methacrylate, 20 parts of neopentyl glycol dimethacrylate, 10 parts of 2,2,4_trimethyl_dimethacrylate into the kneader 1,3-pentanediol ester as acrylic resin monomer mixture, 15 parts of thickener b prepared above, 320 parts of inorganic filler aluminum hydroxide, 0.9 part of curing agent TBPB, 0.1 part of curing agent cis-butyl peroxide tert-butyl olefinic anhydride, 30 parts of inorganic filler and acrylic resin particles, kneading the above raw materials for 10 minutes to obtain an acrylic molding compound. The molding compound was placed in an oven at 60°C, and it was not sticky even immediately af...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an acrylic artificial stone. The acrylic artificial stone comprises the following components in parts by weight: 40-70 parts of acrylic resin monomers, 10-25 parts of a thickening agent, 200-350 parts of inorganic fillers, 0.01-2 parts of a curing agent and 0-2 parts of an accelerant. The manufacturing method of the pure acrylic artificial stone comprises the following steps: A, preparing the thickening agent; B, kneading; and C, forming. Compared with the prior art, the pure acrylic artificial stone disclosed by the invention has the advantage that thickening performance and storage stability are excellent by mixing the special thickening agent and monomers in the invention; the acrylic artificial stone made of acrylic molding plastics has excellent appearance and performance, and can be used for an industrial purpose.

Description

technical field [0001] The invention relates to a pure acrylic artificial stone and a manufacturing method thereof. Background technique [0002] Molded acrylic artificial stone is prepared by mixing inorganic fillers such as aluminum hydroxide into acrylic resin, this acrylic artificial stone has various excellent functions and properties such as excellent appearance, soft touch, weather resistance and molded products. Other properties, and widely used in countertops such as kitchen counters, laundry and dressing table, waterproof surface and other construction purposes. But the boiling point of acrylic resin is low, which limits its application. [0003] The existing foreign acrylic artificial stone has excellent heat resistance and flexibility, but its molding time is very slow, the production efficiency is low, and the surface effect is not good. At the same time, the existing acrylic artificial stone has excellent performance and appearance, but the preparation proces...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B26/10
Inventor 吴德山董义平
Owner 江门市德山复合材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap