An Ultrasonic Assisted Fine Blanking Process and Its Die

A technology of forming process and forming die, which is applied in the field of fine blanking forming process and its device, can solve the problems of reducing the life of the die, reducing the quality of fine blanking parts, and instability, so as to reduce the deformation resistance of fine blanking and improve the performance of fine blanking , Improve the effect of machining lubrication conditions

Inactive Publication Date: 2015-12-09
WUHAN UNIV OF TECH
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

When the plasticity of the material is poor, the section of the fine blanking part is prone to defects such as tearing and cracking
Sometimes tearing and cracking occur at the same time, resulting in secondary shear planes and secondary cracking defects
These defects will seriously affect the dimensional accuracy of fine blanking parts, the strength of parts and other performance
2) Reduce mold life
On the one hand, this deformation method can improve the smoothness and dimensional accuracy of the blanking section, but on the other hand, it makes the working environment of the fine blanking die very harsh.
In addition, due to the thermal effect and severe friction in the fine blanking process, it is easy to cause side adhesion of the die edge, die bulge, punch die chipping, and plastic instability during production, resulting in a decline in the quality of fine blanking parts and mold failure. worn out, even scrapped
When the plasticity of the material is poor, the mold is more prone to the above defects as the deformation resistance increases

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • An Ultrasonic Assisted Fine Blanking Process and Its Die
  • An Ultrasonic Assisted Fine Blanking Process and Its Die
  • An Ultrasonic Assisted Fine Blanking Process and Its Die

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0025] An ultrasonic-assisted fine blanking forming process, which comprises the following steps:

[0026] 1) Prepare the ultrasonic-assisted fine blanking forming die:

[0027] The ultrasonic-assisted fine blanking forming mold includes an upper template 1, a punch base 2, a pressure backing plate 3, a guide post 5, a V-shaped blank holder 6, a guide sleeve 8, a lower template 9, a punch 16, a die 17, The ejector rod 18; the upper formwork 1 and the lower formwork 9 can move relative to each other (set on the formwork); the pressure backing plate 3 is fixed on the upper formwork 1, and the pressure backing plate 3 is provided with a through hole, and the upper formwork 1 is opened There is a punch seat hole, the punch seat 2 penetrates into the punch seat hole on the upper template 1, the threaded hole at the upper end of the punch seat is connected with the hydraulic plunger on the hydraulic press; the upper end of the guide post 5 is fixed to the upper template 1 , the low...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

The invention relates to an ultrasonic-assisted fine blanking process and device. According to the process, ultrasonic wave is input to a male die during the process of fine blanking to allow the male die to resonate, the bottom of the male die vibrates under high frequency, and accordingly the features of the traditional fine blanking formation are changed and the quality of blanks is improved. Compared to the traditional fine blanking, the ultrasonic-assisted fine blanking process has the advantages that forming property of fine blanking material is improved, flow stress of the material is reduced, and the quality of fine-blanked parts is improved; forming load is reduced, and the service life of the fine blanking die is prolonged. The invention further designs an ultrasonic-assisted fine blanking die device. The ultrasonic-assisted fine blanking process and device is significant to widening the range of fine blanking materials, improving the quality of fine blanks and prolonging the service life of the fine blanking die.

Description

technical field [0001] The invention relates to a fine blanking forming process and a device thereof. Background technique [0002] Fine blanking is an advanced metal plastic forming process. Fine blanking in the usual sense refers to strong edge blanking. Compared with ordinary blanking, one fine blanking can obtain parts with bright blanking section, smooth surface and high dimensional accuracy. Due to its high-quality, high-efficiency and low-consumption characteristics, the fine blanking process has been more and more widely used in the fields of aerospace, machinery, electronics and military industry. Fineblanked parts are widely used for functional parts that require the smallest dimensional tolerances and have the smallest roughness. At present, with the rise of the automobile industry, the application of fine blanking technology in automobiles has also been greatly developed. There are about 40 to 200 fine blanking parts in a car. [0003] At present, fine blankin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B21D28/02B21D28/14B21D45/04B21D37/00
Inventor 刘艳雄华林宋燕利赵新浩
Owner WUHAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com