Powder metallurgy high speed steel and preparation method thereof

A technology of powder metallurgy and high-speed steel, applied in the field of powder metallurgy high-speed steel and its preparation, can solve the problems of high price of powder metallurgy high-speed steel, difficult and expensive control of material impurity content, etc. Performance, the effect of improving hardness

Active Publication Date: 2016-02-24
长沙市萨普新材料有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the current process of powder metallurgy high-speed steel is quite complicated, including smelting, atomization powder making, packaging, hot isostatic pressing and other process steps, which require expensive melting and atomization equipment and hot isostatic pressing equipment, and the material is smelted and prepared In the process, it is difficult to control the impurity content of the material, so the price of powder metallurgy high-speed steel is very expensive

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Powder metallurgy high speed steel and preparation method thereof
  • Powder metallurgy high speed steel and preparation method thereof
  • Powder metallurgy high speed steel and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0041] The preparation methods of powder metallurgy high-speed steel and the powder metallurgy high-speed steel obtained by these methods will be described in detail through experiments. Through these descriptions, those skilled in the art can clearly understand the outstanding features of the powder metallurgy high-speed steel preparation method of the present invention.

[0042] 1. Preparation of powder metallurgy high speed steel

[0043] 1.1. Basic process steps

[0044] 1) Prepare the powder mixture

[0045] Weigh the raw materials according to the set components and proportions, and carry out mixed ball milling for 70-90 hours in a drum ball mill at a ball-to-material ratio (8-10):1, at a speed of 20-40 rpm, to prepare powder mixture;

[0046] 2) Molding

[0047] The powder mixture is made into a compact by cold isostatic pressing, the cold isostatic pressing pressure is 150MPa-350MPa, and the holding time is 1-10 minutes;

[0048] 3) Sintering

[0049] The above-m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
flexural strengthaaaaaaaaaa
flexural strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses powder metallurgy high-speed steel and a preparation method thereof. The method is simpler than the existing powder metallurgy high-speed steel preparation method, steps of high-speed steel mother alloy smelting, atomization for making powder and hot isostatic pressing are omitted, great equipment investment is not needed and the production cost of powder metallurgy high-speed steel is reduced. The impurity content of the powder metallurgy high-speed steel prepared by adopting the method provided by the invention is low and the using performance is excellent. The powder metallurgy high-speed steel provided by the invention is prepared through the steps of 1) preparing powder mixture: weighing raw materials according to set components and proportioning ratio, and mixing and ball-milling the raw materials in a roller-type ball mill to obtain the powder mixture; 2) molding: molding the powder mixture into pressed blanks through cold isostatic pressing; 3) sintering: sintering the pressed blanks in a vacuum or inert gas atmosphere by adopting a hot-pressing sintering technology, heating the pressed blanks to 1100-1250 DEG C during sintering, preserving heat for 30-90 minutes and keeping sintering pressure to be 10-40Mpa; 4) hot forging; 5) heat treatment.

Description

technical field [0001] The invention mainly relates to a powder metallurgy high-speed steel and a preparation method thereof, in particular to an ultra-high alloyed powder metallurgy high-speed steel and a preparation method thereof. Background technique [0002] High-speed steel is the main material for making tools and molds. The traditional metallurgical casting high-speed steel is ledeburite steel, and the steel ingot forms the ledeburite eutectic when it solidifies. The existence of the ledeburst eutectic leads to large and more eutectic carbides in the steel. After rolling or calendering, these Eutectic carbides are still unevenly distributed. With the increase of the alloy content and the increase of the cross-sectional area of ​​the steel, the carbide segregation in the high-speed steel is aggravated, which causes the strength of the high-speed steel to decrease, and it is difficult to make the high-speed steel have good performance. In order to solve this problem,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/00C22C33/02
Inventor 陈豫章李颖
Owner 长沙市萨普新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com