Ethylene-propylene-diene monomer and fluororubber compound sealing gasket material and preparation method thereof

A technology of EPDM rubber and composite gasket, applied in the field of rubber composite material processing, can solve the problems of low strength, unsatisfactory sealing effect, poor wear resistance, etc. Effect

Inactive Publication Date: 2014-04-02
马鞍山市中澜橡塑制品有限公司
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing rubber gaskets have defects such as unsatisfactory sealing effect, p

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ethylene-propylene-diene monomer and fluororubber compound sealing gasket material and preparation method thereof
  • Ethylene-propylene-diene monomer and fluororubber compound sealing gasket material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0009] The present invention will be described in detail below through specific examples.

[0010] A EPDM fluororubber composite gasket material, made of the following parts by weight (kg) of raw materials: EPDM (4045) 100, fluororubber 10, zinc oxide 4, magnesium oxide 8, poly Myristyl acrylate 13, p-tert-butylphenol formaldehyde resin 10, zinc stearate 3, N660 carbon black 40, spray carbon black 45, accelerator CBS 0.5, accelerator M1, accelerator DM2, modified attapulgite 10;

[0011] The modified attapulgite is made of the following parts by weight (kg) of raw materials: attapulgite 20, clay 20, 1,6-hexamethylene diisocyanate 3, tripropylene glycol diacrylate 4, alum 5, iron ore Residue 1, polytetrafluoroethylene 4, silane coupling agent KH-5502, silicon carbide 4, zinc oxide 8, 2,6-di-tert-butyl-p-cresol 1, pepper seed oil 1; the preparation method is attapulgite , Clay and iron slag are mixed and put into a calciner at 700-720℃ for 3-4 hours, cooled, soaked in 10-12% hydroc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an ethylene-propylene-diene monomer and fluororubber compound sealing gasket material which is prepared from the following raw materials in parts by weight: 100-110 parts of ethylene propylene diene monomer (4045), 10-12 parts of fluororubber, 4-6 parts of zinc oxide, 8-10 parts of magnesium oxide, 13-14 parts of tetradecyl methacrylate polymer, 10-12 parts of para-tert-butylphenol formaldehyde resin, 3-4 parts of zinc stearate, 40-45 parts of N660 carbon black, 45-60 parts of spraying carbon black, 0.5-1.5 parts of accelerant CBS (N-Cyclohexy-2-Benzothiazole Sulfonamide), 1-2 parts of accelerant M, 2-3 parts of accelerant DM (dibenzothiazole disulfide) and 10-12 parts of modified attapulgite. According to the ethylene-propylene-diene monomer and fluororubber compound sealing gasket material, by adding the modified attapulgite, the process property of a rubber material is improved; by using an environment-friendly compounding agent, the toxic and side effects and the pollution to the environment are reduced. The ethylene-propylene-diene monomer and fluororubber compound sealing gasket material is reasonable in formula, simple in process and low in cost and has better oil resistance and sealing property.

Description

technical field [0001] The invention relates to the field of processing rubber composite materials, in particular to an EPDM fluorine rubber composite gasket material and a preparation method thereof. Background technique [0002] Gasket is a material used for sealing inside machinery, equipment, pipelines, etc. The gaskets currently used are mostly rubber gaskets, which are characterized by high temperature resistance, ozone resistance, natural aging resistance, vacuum resistance, fuel oil resistance, lubricating oil resistance, strong oxidant resistance, chemical resistance and good electrical insulation performance. Widely used in defense industry and civilian industry. However, the existing rubber gaskets have defects such as unsatisfactory sealing effect, poor wear resistance and low strength, which are far from meeting the actual requirements. Therefore researching and developing a kind of high-performance rubber gasket has become the task of top priority. Contents...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/16C08L27/12C08L33/10C08L61/10C08K13/06C08K9/06C08K3/34C08K3/22C08K5/098C08K3/04
CPCC08L23/16C08L2205/035C08L27/12C08L33/10C08L61/06C08K13/06C08K9/06C08K3/346C08K2003/2296C08K2003/222C08K5/098C08K3/04
Inventor 陈贤锋阚蕾申大伟沈根骆敏申丽霞陈玉娟沈春花沈红梅
Owner 马鞍山市中澜橡塑制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap