Special adhesive of cloth stamping coating material

A kind of adhesive and special technology, applied in the direction of coating, textile and paper making, fiber processing, etc., can solve the problem of release agent, colorant, adhesive stability, heat resistance and weather resistance are not ideal, restricting anodized aluminum Manufacturing development, poor matching and other problems, to achieve the effect of good product stability, wide application range and simple production process

Inactive Publication Date: 2014-04-02
孙光华
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the wide variety of anodized aluminum coatings, the compatibility between them is not good; and the stability, heat resistance, and weather resistance of the raw materials such as release agents, colorants, and adhesives used are not ideal. To a large extent, it restricts the development of the electrochemical aluminum manufacturing industry

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0011] In an embodiment, the special adhesive includes the following formula: 5-30% styrene resin, 70-95% solvent.

[0012] A method for preparing the above-mentioned special adhesive, the method comprises the following processing steps:

[0013] 1. According to the formula, first weigh the solvent and pour it into the reaction kettle, and stir it under normal temperature and pressure;

[0014] 2. Then add styrene resin into the square kettle and stir for 1 to 2 hours;

[0015] 3. Measure the solid content (5-30%) after all the solids are dissolved, and make corresponding adjustments by adding relevant solvents according to the theoretical value;

[0016] 4. Stir slowly for another half an hour, and finally weigh and pack.

[0017] The solvent includes two or more of ethyl ester, toluene, butyl ester and methanol.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention discloses a special adhesive of a cloth stamping coating material. The special adhesive comprises, by weight, 5-30 parts of a styrene resin and 70-95 parts of a solvent, wherein the solvent comprises two or more than two materials selected from ethyl ester, toluene, butyl ester and methanol. The special adhesive has characteristics of simple production process, good product stability, wide application range and the like, and provides good adhesion with aluminum layers, coated fabrics, and a plurality of PVC leathers.

Description

technical field [0001] The invention relates to a special adhesive for ironing cloth coating. Background technique [0002] Anodized aluminum foil can replace metal foil as a decorative material, mostly gold and silver. It has the characteristics of gorgeous appearance, bright color, dazzling crystal, easy to use, etc. It is suitable for hot stamping on paper, textiles, plastics, leather, coated fabrics, plexiglass, plastics and other materials. It is the most commonly used material for modern hot stamping and binding, and the demand is huge. However, due to the wide variety of anodized aluminum coatings, the compatibility between them is not good; and the stability, heat resistance, and weather resistance of the raw materials such as the release agent, colorant, and adhesive used are not ideal. To a large extent, it restricts the development of the electrochemical aluminum manufacturing industry. Contents of the invention [0003] The first technical problem to be solv...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D125/04D06M15/233
Inventor 孙光华
Owner 孙光华