Preparation method of multilayer PEG-DMA hydrogel

A PEG-DMA and hydrogel technology, applied in the field of preparation of PEG-DMA hydrogel, can solve the problems of detachment, instability, poor mechanical strength, etc., and achieve the effects of good flexibility, avoidance of deformation, and simple structure

Active Publication Date: 2015-07-15
GUANGDONG XIAN JIAOTONG UNIV ACADEMY +1
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the PEG-DMA hydrogels used in tissue engineering are all single-layer and isotropic, however, biological tissues (such as skin, etc.) are usually multi-layer and anisotropic, and the existing single-layer PEG -DMA hydrogels are difficult to meet the anisotropic requirements of biological tissues
However, since PEG-DMA hydrogel is a kind of water-containing biosoft material, it is soft, not easy to adhere, and has poor mechanical strength, so it is very easy to damage, deform, and damage between layers when building a multilayer structure. It is difficult to construct a stable multi-layer PEG-DMA hydrogel structure due to falling off and unstable combination

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of multilayer PEG-DMA hydrogel
  • Preparation method of multilayer PEG-DMA hydrogel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Example 1: Preparation of double-layer PEG-DMA hydrogel

[0034] Take two glass clips, a U-shaped silicone rubber strip with a thickness of 2mm and several fixing clips, place the U-shaped silicone rubber strip between the two glass clips, and then use the fixing clips to connect the glass clips to the silicone rubber. The strips are clamped to make a U-shaped single-layer mold with a thickness of 2mm.

[0035] Add 20mL of deionized water and 2g of PEG-DMA into a beaker, stir well to obtain a PEG-DMA solution with a mass concentration of 10%; then add 0.1mL of 2-hydroxy-2-methylpropiophenone, and wrap the beaker with tin foil to avoid The first layer of PEG-DMA solution was prepared by light stirring for more than 30 minutes; the first layer of PEG-DMA solution was injected into a U-shaped single-layer mold with a syringe, and then placed in an ultraviolet crosslinking apparatus for light crosslinking for 2 minutes to obtain The first layer of PEG-DMA hydrogel with a m...

Embodiment 2

[0039] Example 2: Preparation of double-layer PEG-DMA hydrogel

[0040] Take two glass clips, a U-shaped silicone rubber strip with a thickness of 2mm and several fixing clips, place the U-shaped silicone rubber strip between the two glass clips, and then use the fixing clips to connect the glass clips to the silicone rubber. The strips are clamped to make a U-shaped single-layer mold with a thickness of 2mm.

[0041] Add 20mL of deionized water and 2g of PEG-DMA into a beaker, stir well to obtain a PEG-DMA solution with a mass concentration of 10%; then add 0.1mL of 2-hydroxy-2-methylpropiophenone, and wrap the beaker with tin foil to avoid The first layer of PEG-DMA solution was prepared by light stirring for more than 30 minutes; the first layer of PEG-DMA solution was injected into a U-shaped single-layer mold with a syringe, and then placed in an ultraviolet crosslinking apparatus for light crosslinking for 2 minutes to obtain The first layer of PEG-DMA hydrogel with a m...

Embodiment 3

[0045] Example 3: Preparation of double-layer PEG-DMA hydrogel

[0046] Take two glass clips, a U-shaped silicone rubber strip with a thickness of 4mm and several fixing clips, place the U-shaped silicone rubber strip between the two glass clips, and then use the fixing clips to connect the glass clips to the silicone rubber. Clamp the bar to make a U-shaped single-layer mold with a thickness of 4mm.

[0047] Add 20mL of deionized water and 3g of PEG-DMA into a beaker, stir well to obtain a PEG-DMA solution with a mass concentration of 15%; then add 0.1mL of 2-hydroxy-2-methylpropiophenone, and wrap the beaker with tin foil to avoid The first layer of PEG-DMA solution was prepared by light stirring for more than 30 minutes; the first layer of PEG-DMA solution was injected into a U-shaped single-layer mold with a syringe, and then placed in an ultraviolet crosslinking apparatus for light crosslinking for 2 minutes to obtain The first layer of PEG-DMA hydrogel with a mass conce...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a multilayer PEG-DMA hydrogel. The preparation method comprises the following steps: 1) taking PEG-DMA, and adding into deionized water to uniformly stir to prepare a first-layer PEG-DMA solution; (2) adding an evocating agent into the first-layer PEG-DMA solution prepared in the step (1), uniformly stirring while keeping out of the sun, feeding into a mold, and performing ultraviolet illumination cross-linking to prepare a first-layer PEG-DMA hydrogel; (3) taking the PEG-DMA, adding into the deionized water to uniformly stir to prepare a second-layer PEG-DMA solution; (4) adding the evocating agent into the second-layer PEG-DMA solution prepared in the step (3), uniformly stirring while keeping out of the sun, feeding into the mold filled with the first-layer PEG-DMA hydrogel, and performing ultraviolet illumination cross-linking to prepare a double-layer PEG-DMA hydrogel; (5) repeating the steps (3) and (4) to prepare the multilayer PEG-DMA hydrogel. By adopting the preparation method provided by the invention, a stable multilayer PEG-DMA hydrogel structure with anisotropism can be constructed.

Description

technical field [0001] The invention relates to a preparation method of PEG-DMA hydrogel, in particular to a preparation method of multilayer PEG-DMA hydrogel. Background technique [0002] In recent years, biomaterials have been widely used in various fields, and hydrogel, as a typical biomaterial, has good biocompatibility, water content, softness, degradability, ease of preparation, The excellent performance such as sensitivity to external stimuli has been widely used in cell culture, tissue engineering, biosensors and actuators, drug release systems and other fields. PEG-DMA (polyethylene glycol dimethacrylic acid) is a hydrogel with PEG (polyethylene glycol) macromonomer, due to its good biocompatibility, non-toxic, non-volatile, stable Good performance, and the mechanical properties parameters (elastic modulus, Poisson's ratio) are close to some tissues of the human body (such as skin, muscle tissue) and the advantages of modifiability make it popular and widely used ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B32B27/06B32B27/16B32B27/28C08J3/28C08J3/24
Inventor 徐峰何翔王琳王鹏飞黄国友卢天健
Owner GUANGDONG XIAN JIAOTONG UNIV ACADEMY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com