A kind of preparation method of cross-linked chitosan/hyaluronic acid composite porous scaffold

A technology of cross-linking chitosan and hyaluronic acid, which is applied in the fields of medical science and prostheses, can solve the problems of weak mechanical strength, achieve good mechanical properties, facilitate proliferation and differentiation growth, and have high porosity

Inactive Publication Date: 2015-08-19
TONGJI UNIV
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Based on the advantages of convenience, easy access, taking from nature and using in nature, taking advantage of the similarity and compatibility between natural biological materials and human tissues, many researchers have chosen natural biological materials to prepare tissue engineering scaffold materials, but natural biological materials The problem of weak mechanical strength generally exists, which requires people to choose suitable natural biomaterials for blending and compounding, and to select effective cross-linking agents to improve their mechanical properties. The cross-linking agent must also be non-cytotoxic

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of cross-linked chitosan/hyaluronic acid composite porous scaffold
  • A kind of preparation method of cross-linked chitosan/hyaluronic acid composite porous scaffold

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] The methanol suspension of 2% chitosan, the methanol suspension of hyaluronic acid and the methanol solution of silane coupling agent KH-560 were configured respectively;

[0024] The methanol suspension of chitosan, the methanol suspension of hyaluronic acid and the methanol solution of silane coupling agent KH-560 were blended at a mass ratio of 35:35:30, heated to 70°C, and stirred for 3 hours. Suction filtration, repeated washing with anhydrous methanol until the unreacted silane coupling agent KH-560 is washed away, and vacuum-dried at 60°C for 24 hours to obtain a cross-linked chitosan / hyaluronic acid composite material;

[0025] With above-mentioned cross-linked chitosan / hyaluronic acid composite material, be dissolved in 100g distilled water, prepare the aqueous solution that mass percent is 1% cross-linked chitosan / hyaluronic acid composite material, defoaming, obtain the deaeration after Aqueous solution of cross-linked chitosan / hyaluronic acid composite;

[...

Embodiment 2

[0029] Same as Example 1, but the methanol suspension of chitosan, the methanol suspension of hyaluronic acid and the concentration of the methanol solution of silane coupling agent KH-560 in step (1) all become 3% by 2%, other constant.

Embodiment 3

[0031] Same as Example 1, but the methanol suspension of chitosan in step (1), the methanol suspension of hyaluronic acid and the concentration of the methanol solution of silane coupling agent KH-560 all become 1% by 2%, other constant.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
porosityaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of new materials and relates to a preparation method of a crosslinked chitosan / hyaluronic acid compound porous scaffold. According to the preparation method, natural biological materials such as chitosan and hyaluronic acid are used as raw materials and an organic silane coupling agent KH-560 is used as a crosslinking agent, and the crosslinked chitosan / hyaluronic acid compound porous scaffold which is made of purely natural biological materials and is excellent in mechanical property is prepared adopting a freeze-drying method. The crosslinked chitosan / hyaluronic acid compound porous scaffold prepared by adopting the preparation method has the characteristics of high porosity, high pores strength, large pores diameter and the like, is of an open type pore structure that small pores are contained in large pores, and is suitable for planting cells on the surface of the scaffold, wherein the pore diameter is 100-300 mu m and porosity is more than 90%. Compared with a chitosan scaffold, the crosslinked chitosan / hyaluronic acid compound porous scaffold has the advantages that the mechanical property is better; proliferation and differentiation effect of the cells on the surface of the porous scaffold is better due to the addition of the organic silane coupling agent, and affinity to biological cells is better.

Description

technical field [0001] The invention belongs to the technical field of new materials, and in particular relates to a preparation method of a cross-linked chitosan / hyaluronic acid composite porous support. Background technique [0002] The emergence of tissue engineering has brought bright prospects for human health and life extension. The use of biomedical materials to prepare artificial substitutes to treat diseases can solve the problem that human organs need to be replaced due to defects or loss of function, but the materials are limited. When people put their energy into artificial tissues or organs, one of the keys is the preparation of three-dimensional porous scaffold materials for tissue engineering using cell culture. [0003] At present, porous scaffold materials for tissue engineering are mainly derived from some natural polymers and synthetic polymers. Natural polymers mainly include collagen, chitin, chitosan, hyaluronic acid, gelatin, alginate, chondroitin sul...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08J9/28C08J3/24C08L5/08C08K5/5435A61L27/20A61L27/56
Inventor 杨正龙
Owner TONGJI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products