Pressure cooling process of hot-formed steel plate segment strengthening parts and press servo ejector device

A segmented strengthening and hot forming technology, applied in the field of high-strength steel stamping, can solve problems such as complex structure, and achieve the effect of unified processing technology, simple structure and protection of human safety.

Active Publication Date: 2016-04-27
WUXI LANGXIAN LIGHTWEIGHT TECH CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0017] But the defect of this technology is: from the point of view, this method is an improvement to the conventional practice of the existing soft zone technology - heating the mold to 370-700 ° C - in order to reduce the wear of the mold in production after heating, Or reduce the heating equipment, but still need to heat the mold, which belongs to the temperature control technology of the cooling medium
In terms of mold structure, this technology requires a heating device inside the active punch and die, so the structure is complicated

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Pressure cooling process of hot-formed steel plate segment strengthening parts and press servo ejector device
  • Pressure cooling process of hot-formed steel plate segment strengthening parts and press servo ejector device
  • Pressure cooling process of hot-formed steel plate segment strengthening parts and press servo ejector device

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0061] Such as Figure 3-Figure 5 As shown, the workpiece is 1.8mm thick, 150mm wide, and 1000mm long hot-formed boron steel workpiece section forming and quenching diagram. The workpiece product requirement is f 6 The corresponding product area is HS400 soft area, and the rest are hard area HS1150. The concrete preparation process schematic diagram of this method, wherein:

[0062] image 3 In its original state, according to Figure 3-Figure 5 It can be seen that the device for realizing the method includes: an upper die 1, a lower die 2, an upper servo ejector pin 3 on a press, a lower servo ejector pin 4 on a press, an upper die pressing core 5, a lower die pressing core 6, and an upper workbench ( Slide block) 7, workbench 8 under the press.

[0063] The upper mold 1 covers the range of HS1150 in the hard area of ​​the product, and the material is high-quality mold steel SKD61;

[0064] The upper mold pressing material core 5 covers the product soft zone HS400 range...

Embodiment 2

[0076] Such as Figure 3-Figure 5 As shown, the workpiece is 1.8mm thick, 150mm wide, and 1000mm long hot-formed boron steel workpiece section forming and quenching diagram. The workpiece product requirement is f 6 The corresponding product area is HS400 soft area, f 8 except f 6 Outside the area is the soft area HS700, and the rest of the product area is the hard area HS1150.

[0077] This method realizes the device such as image 3 shown, where:

[0078] The upper mold 1 covers all areas of the product soft area HS700 and hard area HS1150, and the material is high-quality die steel SKD61;

[0079] The upper mold pressing material core 5 covers all areas of the soft area HS700 of the product, and the material is high-quality mold steel SKD61;

[0080] The lower mold pressing material core 6 covers all areas of the product soft zone HS400 and soft zone HS700, and the material is high-quality mold steel SKD61;

[0081] The lower mold 2 covers all areas of the hard area H...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
strengthaaaaaaaaaa
plasticityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a pressure cooling process of segmented reinforcing type parts of a hot forming steel plate, and pressing machine servo ejector rod devices. Through the independent pressing machine servo ejector rod devices, the magnitude of loading force borne by a workpiece and / or force bearing and pressure keeping time for the workpiece are adjusted, and therefore the cooling speed of each sub-area of the workpiece is controlled, different types of material mechanical performance of the sub-areas of the workpiece are obtained. Required material characteristics can be achieved for any area according to the design requirements, no additional die heating device needs to be arranged, and production cost and procedure complexity are greatly reduced.

Description

technical field [0001] The invention relates to a method in the technical field of high-strength steel stamping, in particular to a pressure cooling process and a servo ejector rod servo device for a segmentally strengthened hot-formed steel plate with a strength of about 1500 MP. Background technique [0002] As a new type of ultra-high-strength hot-formed steel plate, automotive boron steel plate provides the possibility for segmental strengthening technology—the same part can adopt different heat treatment processes in different regions of the part according to the needs of automobile design, so as to obtain different strength and plasticity. The production process of the soft zone technology for hot-formed boron steel materials is divided into 4 stages: [0003] 1) Heating: heating the boron steel plate to the temperature required for heat treatment; [0004] 2) Transmission: transfer the boron steel plate to the die to be stamped; [0005] 3) Forming: Stamping and fo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B21D22/02B21D37/16
Inventor 陈扬
Owner WUXI LANGXIAN LIGHTWEIGHT TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com