High-tensile hot-rolled steel sheet and manufacturing method thereof

A hot-rolled steel plate, high-tension technology, applied in the direction of manufacturing tools, metal rolling, chemical instruments and methods, etc., can solve problems such as distortion of parts, and achieve the effect of good workability and excellent material stability.

Active Publication Date: 2016-03-02
JFE STEEL CORP
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, if steel plates with different local strengths are press-formed, the amount of springback will change in proportion to the strength, and the parts will be distorted.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-tensile hot-rolled steel sheet and manufacturing method thereof
  • High-tensile hot-rolled steel sheet and manufacturing method thereof
  • High-tensile hot-rolled steel sheet and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0094] Molten steel having the composition shown in Table 1 was smelted and continuously cast by a generally known method to produce a billet (steel material) with a wall thickness of 250 mm. These billets were heated to 1250° C., rough rolling and finish rolling were performed, and after finish rolling, they were cooled and coiled to produce hot-rolled steel sheets with a thickness of 2.3 mm and a width of 1400 mm. Table 2 shows the finish rolling temperature, the average cooling rate of cooling (the average cooling rate from the finish rolling temperature to the coiling temperature) and the coiling temperature of the above-mentioned finish rolling.

[0095] Next, a part of the hot-rolled steel sheets (hot-rolled numbers in Table 2: 3, 9, and 11) obtained as above were pickled to remove surface scale, and then annealed (annealing temperature: 680° C., Holding time: 120 seconds), dipped in a hot-dip galvanizing bath (bath composition: 0.1% Al-Zn, bath temperature: 480°C), form...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
hardnessaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The present invention provides a high-tensile hot-rolled steel sheet having both high strength and good workability (stretch-flangeability) and excellent material uniformity, and a method for producing the same. A hot-rolled steel sheet having a tensile strength of 780 MPa or more, comprising, in mass %, C: 0.03% to less than 0.07%, Si: 0.3% or less, Mn: 0.5% to 2.0% or less, and P: 0.025 % or less, S: 0.005% or less, N: 0.0060% or less, Al: 0.1% or less, Ti: 0.07% or more and 0.11% or less, V: 0.08% or more and less than 0.15%, and Ti and V satisfy 0.18≤Ti +V ≤ 0.24 (Ti, V: content of each element (mass %)), the balance contains Fe and unavoidable impurities; a matrix with an area ratio of ferrite phase to the overall structure of 95% or more; and Ti and V with an average particle diameter of less than 10 nm dispersed and precipitated, and the volume ratio of the fine carbides to the total structure is 0.0020 or more.

Description

technical field [0001] The present invention relates to a tensile material suitable for raw materials such as transportation equipment parts such as automobile parts and structural parts, which has excellent processability, especially excellent stretch flangeability, and is also excellent in material stability and material uniformity. Strength (TS): High-tensile hot-rolled steel sheet above 780MPa and its manufacturing method. Background technique [0002] From the viewpoint of global environmental protection, in order to reduce CO 2 In terms of emissions, it is necessary to reduce the weight of the car body while maintaining the strength of the car body, thereby improving the fuel efficiency of the car, which has become a very important issue in the automotive industry. In order to reduce the weight of an automobile body while maintaining its strength, it is effective to increase the strength of a steel sheet used as a raw material for automobile parts to reduce the thickn...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/00B21B1/26C21D9/46C22C38/14C22C38/60
CPCC21D9/46C22C38/14B32B15/013C22C18/04C22C38/001C22C38/02C22C38/04C22C38/06C22C38/12C21D8/0426C21D8/0463C21D8/0478C21D2211/004C21D2211/005Y10T428/12799C22C38/00C23C2/024C23C2/02C23C2/0224C22C38/60C21D8/0263C22C38/002C22C38/008C22C38/08C22C38/10C22C38/16C22C38/24C22C38/26C22C38/28
Inventor 有贺珠子船川义正森安永明
Owner JFE STEEL CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com