Wet lay-up process for epoxy terrazzo floor

A technology of epoxy water and wet laying, which is applied in the construction field of epoxy terrazzo, can solve the problems of waste and unqualified technical materials, and achieve the effects of material saving, smooth structure and cost reduction

Inactive Publication Date: 2014-09-10
宿州典跃新型建筑材料有限公司
View PDF5 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is to provide a wet laying process of epoxy terrazzo floor to overcome defects such as unqualified existing technology and waste of technical materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] (1) By weight percentage: 20% of 8-30 mesh sand and gravel, 40% of 30-80 mesh sand and gravel, and 40% of 80-200 mesh sand and gravel are intermixed into graded sand, and the sand and stone are selected from natural quartz sand, Natural quartz colored sand and stained glass;

[0022] (2) By weight, 60% of epoxy resin, 3% of reactive diluent, 20% of 400-1000 mesh quartz powder, 14% of color paste and 3% of auxiliary agent are mixed to prepare epoxy resin material; 5 parts of epoxy resin material and 1 part of weather-resistant alicyclic amine modified curing agent are mixed evenly to form an epoxy resin mixture;

[0023] (3) In parts by weight, add 6 parts of graded sand to the stirring device and stir for 10 minutes, then add 1 part of epoxy resin mixture, and stir for 15 minutes;

[0024] (4) Spread the mixture that step (3) obtains on the base layer to be constructed, the thickness of the mixture is 15mm, level the ground, then smooth it, and compact the sand materia...

Embodiment 2

[0029] (1) Calculated by weight percentage: 10% of 8-30 mesh sandstone, 30% of 30-80 mesh sandstone, and 60% of 80-200 mesh sandstone are intermixed into graded sand, and the sandstone is selected from natural quartz sand, Natural quartz colored sand and stained glass;

[0030] (2) By weight, 50% of epoxy resin, 5% of reactive diluent, 33% of 400-1000 mesh quartz powder, 10% of color paste and 2% of auxiliary agent are mixed to prepare epoxy resin material; 4 parts of epoxy resin material and 1 part of weather-resistant alicyclic amine modified curing agent are mixed uniformly to form an epoxy resin mixture;

[0031] (3) In parts by weight, add 5 parts of graded sand to the stirring device and stir for 8 minutes, then add 1 part of epoxy resin mixture, and stir for 8 minutes;

[0032] (4) spread the mixture that step (3) obtains on the base layer to be constructed, the thickness of the mixture is 20mm, level the ground, then trowel, and compact the sand material;

[0033] (5...

Embodiment 3

[0037] (1) Calculated by weight percentage: 15% of 8-30 mesh sandstone, 35% of 30-80 mesh sandstone, and 50% of 80-200 mesh sandstone are intermixed into graded sand, and the sandstone is selected from natural quartz sand, Natural quartz colored sand and stained glass;

[0038] (2) By weight, 40% of epoxy resin, 10% of active diluent, 37% of 400-1000 mesh quartz powder, 12% of color paste and 1% of auxiliary agent are mixed to prepare epoxy resin material; 5 parts of epoxy resin material and 1 part of weather-resistant alicyclic amine modified curing agent are mixed evenly to form an epoxy resin mixture;

[0039] (3) In parts by weight, add 6 parts of graded sand to the stirring device and stir for 5 minutes, then add 1 part of epoxy resin mixture, and stir for 12 minutes;

[0040] (4) spread the mixture that step (3) obtains on the base layer to be constructed, and the thickness of the mixture is 5mm to level the ground, then trowel, and compact the sand material;

[0041] ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of epoxy terrazzo construction and discloses a wet lay-up process for an epoxy terrazzo floor. The wet lay-up process comprises the steps of (a) grading sand and stone to obtain graded sand; (2) uniformly mixing the epoxy resin material and a curing agent to obtain an epoxy resin mixture; (3) adding the graded sand to a stirring device in which epoxy terrazzo is filled and stirring, then adding the epoxy resin mixture and uniformly stirring; (4) spreading the mixture on a road bed to be constructed, then leveling the floor, finishing and compacting the sand material; (5) after the mixture is completely hardened, grouting with the epoxy resin mixture so that the voids in the floor is completely filled; and (6) after the epoxy resin mixture is completely hardened, polishing the floor. The wet lay-up process disclosed by the invention is simple, the effective conservation of materials is achieved, and the fabricated epoxy terrazzo floor has the characteristics of smooth structure, dust-proof and moisture-proof properties and wear resistance.

Description

technical field [0001] The invention relates to the technical field of epoxy terrazzo construction, in particular to a wet laying process of epoxy terrazzo floor. Background technique [0002] Epoxy terrazzo is a seamless decorative floor that incorporates recycled clear glass or granite, flint or other aggregates. The predecessor of epoxy terrazzo floor can be traced back to the terrazzo floor in ancient Rome. Its shocking appearance, wear-resistant and flexible qualities are favored and inherited by forward-looking architects who established the first modern empire. With the modern and fast-paced lifestyle, the epoxy terrazzo floor presents an impressive ground effect and has become the first choice of designers around the world. The current factory buildings and parking lots all need floors, and different occasions require floors with different performances. Many of the current floors use the same process and cannot be made according to demand. Therefore, either the te...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/14C04B111/60
Inventor 郭君建汝宗林
Owner 宿州典跃新型建筑材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com