Method for producing aerated building block by using doping blast furnace slag

A technology for aerated blocks and blast furnace slag is applied in the field of producing aerated blocks by doping blast furnace slag, and achieves the effects of large usage amount, light bulk density and high strength

Inactive Publication Date: 2014-09-17
HEFEI RISINE HEATEK
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In summary, there have been reports on the use of blast furnace slag as an auxiliary raw material to produce cement, wall bricks, and road materials, but there have been no reports on the use of blast furnace slag as the main raw material for the production of aerated blocks.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0019] A method for producing an aerated block doped with blast furnace slag, the method includes the following steps:

[0020] 1), after the fly ash, dihydrate gypsum and blast furnace slag are mixed and crushed, 12-19 parts of fly ash, 2-3 parts of dihydrate gypsum and 20-30 parts of blast furnace slag are taken in parts by mass;

[0021] 2) Take 10-15 parts of vanadium slag and 1-2.5 parts of aluminum powder in mass parts before fine grinding, and mix the crushed fly ash, dihydrate gypsum and blast furnace slag with vanadium slag and aluminum powder evenly After fine grinding, the crushed fly ash, dihydrate gypsum and blast furnace slag are evenly mixed with vanadium slag and aluminum powder, and the particle size of fine grinding is less than 20mm;

[0022] 3), crushing the crushed stones, and taking 12-25 parts by mass of the crushed stones;

[0023] 4), put the crushed crushed stones and the finely ground dry material into the mixing equipment, add water to fully stir,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for producing an aerated building block by using doping blast furnace slag. The method comprises the following steps: 1) mixing and crushing fly ash, dihydrate gypsum and blast furnace slag and weighing, by mass, 12 to 19 parts of fly ash, 2 to 3 parts of dihydrate gypsum and 20 to 30 parts of blast furnace slag; 2) before fine grinding, weighing 10 to 15 parts by mass of vanadium slag and 1 to 2.5 parts by mass of aluminum powder, uniformly mixing crushed fly ash, dihydrate gypsum and blast furnace slag with vanadium slag and aluminum powder and then carrying out fine grinding; and 3) crushing broken stone granules and taking 12 to 25 parts by mass of the crushed broken stone granules.

Description

technical field [0001] The invention relates to the field of new building materials, in particular to a method for producing aerated blocks by doping blast furnace slag. Background technique [0002] For a long time, the comprehensive utilization of blast furnace slag has been a worldwide problem. Although a lot of research has been done on the comprehensive utilization of blast furnace slag at home and abroad, most of them have not been implemented in industry due to various technical and economic reasons. [0003] In summary, there have been reports of using blast furnace slag as auxiliary raw material to produce cement, wall bricks, and road materials, but there has been no report of using blast furnace slag as the main raw material for the production of aerated blocks. Contents of the invention [0004] The purpose of the present invention is to provide a method of doping blast furnace slag to produce aerated blocks. The consumption of blast furnace slag is large, ener...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B38/02C04B28/08
Inventor 张时利王建跃王皓静
Owner HEFEI RISINE HEATEK
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products