A kind of acidified mesoporous wo3/sio2 multi-component colloidal ball and its application

A colloidal ball, multi-component technology, applied in chemical/physical process, organic chemistry, carboxylate preparation, etc., to achieve the effect of high catalytic efficiency and low environmental pollution

Active Publication Date: 2016-03-16
ANHUI UNIVERSITY OF TECHNOLOGY
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

(JulienPolleux,et.al.,Template-FreeSynthesisandAssemblyofSingle-CrystallineTungstenOxideNanowiresandtheirGas-SensingProperties,Angew.Chem.Int.Ed.2005,44,267-271.)与本专利接近的文献报道有:Wu等人(Effectsoftungstenoxideontheactivityandthermalstabilityofasulfate-derivedtitaniasupportedplatinumcatalystforpropaneoxidation)用等 Multicomponent Pt / WO prepared by volume impregnation method 3 / TiO 2 Catalyst, Zhang et al. (L.Zhang, et.al., FacilesynthesisandphotocatalyticactivityofhierarchicalWO 3 core-shellmicrospheres, Applied Surface Science, 2011, 258, 1719-1724) prepared core-shell WO 3 Microspheres, and Liu et al. (J.Liu, et.al., NovelMoO 3 andWO 3 hollownospheresassembledwithpolymericmicelles, Materials Letters, 2012,66,25-28) prepared WO 3 Hollow balls, they either put WO 3 Loaded on a carrier with a relatively large specific surface area, or to prepare WO of different forms 3 , while the acidified mesoporous WO 3 / SiO 2 Multi-component colloidal balls have not been reported

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of acidified mesoporous wo3/sio2 multi-component colloidal ball and its application
  • A kind of acidified mesoporous wo3/sio2 multi-component colloidal ball and its application
  • A kind of acidified mesoporous wo3/sio2 multi-component colloidal ball and its application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] 1# acidified mesoporous WO 3 / SiO 2 The concrete preparation steps of multi-component colloidal ball catalyst are as follows:

[0036] (1) Preparation of cetyltrimethylammonium phosphotungstate

[0037] Measure 100mL of absolute ethanol into a beaker, add 0.44g of cetyltrimethylammonium bromide (CTAB), stir until CTAB is completely dissolved, measure 50mL of absolute ethanol into another beaker, add 1.15g For phosphotungstic acid, stir with a glass rod until the phosphotungstic acid is completely dissolved. While stirring, use a dropper to add the phosphotungstic acid solution to the CTAB solution dropwise. After the addition is complete, continue to stir for half an hour to make it fully react. After filtering and drying, the product hexadecyltrimethylphosphotungstic acid quaternary ammonium was obtained, which was designated as W-6.

[0038] (2) WO 3 / SiO 2 Preparation of multi-component colloidal spheres

[0039] Weigh 200mgW-6 and 110mgCTAB into a round botto...

Embodiment 2

[0045] 2# acidified mesoporous WO 3 / SiO 2 The concrete preparation steps of multi-component colloidal ball catalyst are as follows:

[0046] (1) Preparation of W-6

[0047] With the preparation method of W-6 among the embodiment 1.

[0048] (2) WO 3 / SiO 2 Preparation of multi-component colloidal spheres

[0049] Weigh 200mgW-6 and 110mgCTAB into a round bottom flask, add 20mL absolute ethanol, disperse in ultrasonic for 30min, until the solid is completely dispersed, add 80mL distilled water dropwise, and keep stirring at 28°C. After stirring for 6 hours, add 0.3mL ammonia water and 0.5mLTEOS, continue stirring at constant temperature for 16 hours, filter and dry to obtain WO 3 / SiO 2 Multi-component colloidal balls.

[0050] (3) Mesoporous WO 3 / SiO 2 Preparation of multi-component colloidal spheres

[0051] With the preparation method of step (3) in the embodiment 1.

[0052] (4) Acidified mesoporous WO 3 / SiO 2 Preparation of multi-component colloidal spheres ...

Embodiment 3

[0055] 3# acidified mesoporous WO 3 / SiO 2 The concrete preparation steps of multi-component colloidal ball catalyst are as follows:

[0056] (1) Preparation of W-6

[0057] With the preparation method of W-6 among the embodiment 1.

[0058] (2) WO 3 / SiO 2 Preparation of multi-component colloidal spheres

[0059] Weigh 200mgW-6 and 110mgCTAB into a round bottom flask, add 20mL absolute ethanol, disperse in ultrasonic for 30min, until the solid is completely dispersed, add 80mL distilled water dropwise, and keep stirring at 28°C. After stirring for 6 hours, add 0.3mL ammonia water and 0.4mLTEOS, continue to stir at constant temperature for 16 hours, filter and dry to obtain WO 3 / SiO 2 Multi-component colloidal balls.

[0060] (3) Mesoporous WO 3 / SiO 2 Preparation of multi-component colloidal spheres

[0061] With the preparation method of step (3) in the embodiment 1.

[0062] (4) Acidified mesoporous WO 3 / SiO 2 Preparation of multi-component colloidal spheres...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
pore sizeaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses an acidified mesoporous WO3 / SiO2 multi-component colloidal sphere, belonging to the field of chemical catalysts. An active component of the colloidal sphere is SO4<2-> / WO3 / SiO2 of which the structure is like a colloidal sphere; the active component has a mesoporous structure and is high in dispersion property; the particle size is 100-900nm, and the aperture is 3-5nm. The acidified mesoporous WO3 / SiO2 multi-component colloidal sphere disclosed by the invention is used as the catalyst; during catalysis of the esterification reaction between different long-chain fatty acids and alcohols, the acidified mesoporous WO3 / SiO2 multi-component colloidal sphere is excellent in catalyst performance and high in stability. During esterification reaction in which the long-chain fatty acids are oil acids and the alcohols are methanol, and when the using amount of the colloidal sphere catalyst is 3 percent, the esterification rate of the oil acid can reach 97.0 percent; after the oil acids are continuously and cyclically used for 5 times, the conversion rate of the oil acids can be still kept at about 97 percent.

Description

technical field [0001] The invention belongs to the field of chemical catalysts, in particular to an acidified mesoporous WO 3 / SiO 2 Multi-component nanocomposite material and its preparation technology, especially an acidified mesoporous WO with good dispersion, controllable shape and particle size 3 / SiO 2 Multi-component colloidal ball and its preparation technology. The acidified mesoporous WO prepared by the present invention 3 / SiO 2 Multi-component colloidal spheres are used as catalysts to catalyze the esterification of long-chain fatty acids, and have achieved good catalytic effects. Background technique [0002] Multi-component hybrid materials with controllable morphology and composition have great potential application value in the fields of catalysis, solar energy conversion and photoelectric technology (P. Li, et al. Au-ZnOHybrid Nanopyramids and Their Photocatalytic Properties, J. Am. Chem. Soc.2011, 133, 5660-5663; T. Yu, et al. Aqueous Phase Synthesis...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J27/053C07C67/08C07C69/24C07C69/58
Inventor 陈国昌肖标乔红斌裘小宁蒋伟峰吴胜华
Owner ANHUI UNIVERSITY OF TECHNOLOGY