A low-temperature anti-fingerprint surface treatment agent for galvanized steel sheets and an environment-friendly surface treatment galvanized steel sheet

A surface treatment agent, technology of galvanized steel sheet, applied in the direction of metal material coating process, etc., can solve problems such as unsolved problems

Active Publication Date: 2016-12-07
BAOSHAN IRON & STEEL CO LTD +2
View PDF8 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, as a practical problem, the above-mentioned technical problem points have not yet been able to be solved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A low-temperature anti-fingerprint surface treatment agent for galvanized steel sheets and an environment-friendly surface treatment galvanized steel sheet
  • A low-temperature anti-fingerprint surface treatment agent for galvanized steel sheets and an environment-friendly surface treatment galvanized steel sheet
  • A low-temperature anti-fingerprint surface treatment agent for galvanized steel sheets and an environment-friendly surface treatment galvanized steel sheet

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0066] The present invention will be further described below through specific examples.

[0067] The following Examples 1-11 and Comparative Examples 1-7 specifically illustrate the galvanized materials used, the surface cleaning method, the aqueous surface treatment solution and the method for treating galvanized steel sheets.

[0068] 1. Sample

[0069] Galvanized gold-plated steel sheet

[0070]1) Marketed products, plate thickness 0.6mm double-sided galvanized steel (EG) adhesion amount 20g / m 2 ;

[0071] 2) Marketed products, hot-dip galvanized steel (GI) with a plate thickness of 0.6mm have an adhesion of 40g / m 2 ;

[0072] 3) Marketed products, plate thickness 0.6mm hot-dip galvanized steel (GF) adhesion amount 40g / m 2 .

[0073] 2. Cleaning method of metal plate

[0074] The surface of the above-mentioned galvanized steel sheet is cleaned with an aqueous solution (agent concentration: 20g / L) of a medium-alkali degreasing agent (registered trademark: FC-4336, pro...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
minimum film forming temperatureaaaaaaaaaa
Adhesion amountaaaaaaaaaa
Login to View More

Abstract

The invention relates to a low-temperature anti-fingerprint surface treatment agent for galvanized steel sheets and an environment-friendly surface-treated galvanized steel sheet obtained by using the surface treatment agent for surface treatment. The surface of the galvanized steel sheet of the present invention does not contain chromium and does not require high-temperature drying, and can form a surface treatment film under low-temperature drying conditions. The manufacturing process is environmentally friendly and low in energy consumption. The composition of organosilicon compound, titanium compound, vanadium compound and oxidized polyethylene particles (i.e. surface treatment agent) is coated on the surface of galvanized steel sheet, and then dried at a low temperature of 50-75°C, and the surface-treated galvanized steel sheet obtained is simultaneously It has excellent properties such as alkali resistance, solvent resistance, corrosion resistance, fingerprint resistance and coating adhesion.

Description

technical field [0001] The invention belongs to the field of surface treatment of metal materials, and relates to a low-temperature anti-fingerprint surface treatment agent for galvanized steel sheets and an environmentally friendly surface-treated galvanized steel sheet obtained by using the surface treatment agent for surface treatment. The surface of the galvanized steel sheet does not contain chrome and does not require high-temperature drying, the manufacturing process is environmentally friendly and low energy consumption, and the surface-treated galvanized steel sheet also has excellent properties such as alkali resistance, solvent resistance, corrosion resistance, fingerprint resistance and coating adhesion . Background technique [0002] Metal materials such as zinc-containing metal steel sheets and aluminum sheets are widely used in the automobile, building materials, and home appliance industries. However, zinc and aluminum using the above metal materials will be...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23C22/05
Inventor 牟战旗姚勇汤文杰李忠阳贾卫国周阳陈俊袁江南徐强
Owner BAOSHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com