A pressure-sensitive adhesive applied to ultra-thin double-sided adhesive and its preparation method

A double-sided adhesive and pressure-sensitive adhesive technology, applied in the field of pressure-sensitive adhesives, can solve the problems of difficulty in achieving thinning and high adhesion at the same time, and achieve the effects of excellent pressure sensitivity, high adhesion and excellent properties.

Active Publication Date: 2016-10-19
东莞宏石功能材料科技有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, most of the PET double-sided adhesives currently on the market are made of traditional acrylic solvent-based glue, and the thickness is mostly 30~50um. If the coating thickness of acrylic solvent-based glue is reduced, the adhesion will also decrease. The performance requirements of double-sided tape for assembly require at least 1kg / in adhesive force. If traditional acrylic solvent-based glue is used to make double-sided adhesive products with a total thickness of less than 15um, the adhesive force can only reach 500~800g / in. in
Therefore, the existing double-sided tape has the problem that it is difficult to meet the requirements of thinning and high adhesion at the same time, and the above-mentioned problems need to be solved urgently.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0061] The preparation method of the pressure-sensitive adhesive applied to the ultra-thin double-sided adhesive tape of the present embodiment comprises the following preparation steps:

[0062] a, 35 parts of butyl acrylate, 10 parts of 2-ethylhexyl acrylate, 0.5 part of acrylic acid, 1 part of hydroxyethyl acrylate, 30 parts of ethyl acetate and 60 parts of toluene are loaded into a three-neck round bottom flask, and then The three-neck round-bottomed flask is respectively connected with a stirrer, a thermometer, and a condenser, and the above-mentioned raw materials are stirred evenly by the stirrer, and the above-mentioned raw materials are heated by a water bath at the same time;

[0063] b. After heating to 85°C, add a part of 0.3 parts of benzoyl peroxide while stirring;

[0064] c. After adding 0.3 parts of benzoyl peroxide and keeping it at 85°C for 1 hour after heat release, add 0.5 parts of benzoyl peroxide and 4 parts of ethyl acetate to continue the reaction;

...

Embodiment 2

[0069] The preparation method of the pressure-sensitive adhesive applied to the ultra-thin double-sided adhesive tape of the present embodiment comprises the following preparation steps:

[0070] a, 45 parts of butyl acrylate, 20 parts of 2-ethylhexyl acrylate, 2 parts of acrylic acid, 2 parts of hydroxyethyl acrylate, 40 parts of a part of ethyl acetate and 70 parts of toluene are loaded into a three-neck round bottom flask, and then Connect the three-necked round-bottomed flask to a stirrer, a thermometer, and a condenser respectively, and stir the above-mentioned raw materials evenly through the stirrer, and heat the above-mentioned raw materials through a water bath at the same time;

[0071] b. After heating to 86°C, add 1 part of benzoyl peroxide while stirring;

[0072] c. After adding 1 part of benzoyl peroxide and keeping it at 87°C for 0.8 hours after heat release, add 1 part of benzoyl peroxide and 10 parts of ethyl acetate to continue the reaction;

[0073] d. Aft...

Embodiment 3

[0077] The preparation method of the pressure-sensitive adhesive applied to the ultra-thin double-sided adhesive tape of the present embodiment comprises the following preparation steps:

[0078] a, 32 parts of butyl acrylate, 12 parts of 2-ethylhexyl acrylate, 0.7 part of acrylic acid, 1.2 parts of hydroxyethyl acrylate, 34 parts of ethyl acetate and 63 parts of toluene are loaded into a three-necked round bottom flask, and then The three-neck round-bottomed flask is respectively connected with a stirrer, a thermometer, and a condenser, and the above-mentioned raw materials are stirred evenly by the stirrer, and the above-mentioned raw materials are heated by a water bath at the same time;

[0079] b. After heating to 87°C, add 0.4 parts of benzoyl peroxide while stirring;

[0080] c. After adding 0.5 parts of benzoyl peroxide and keeping it at 88°C for 0.6 hours after heat release, add 0.5 parts of benzoyl peroxide and 4 parts of ethyl acetate to continue the reaction;

[0...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
softening pointaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of varnish, in particular to a pressure-sensitive adhesive applied to ultra-thin double-sided adhesives and a preparation method thereof. The pressure-sensitive adhesive applied to ultra-thin double-sided adhesives of the present invention consists of 35-45 parts of butyl acrylate , 10-20 parts of 2-ethylhexyl acrylate, 0.5-2 parts of acrylic acid, 1-2 parts of hydroxyethyl acrylate, 32-50 parts of ethyl acetate, 60-70 parts of toluene, 2-3 parts of dilauryl peroxide Acyl, 5-15 parts of vinyl acetate, 10-30 parts of terpene phenol resin and 0.3-1 part of aluminum acetylacetonate. The pressure-sensitive adhesive finally obtained in the present invention is a two-component cross-linked acrylate pressure-sensitive adhesive, which combines the advantages of acrylate and terpene phenolic resins, so that the double-sided adhesive made of the pressure-sensitive adhesive of the present invention Adhesive, when the total thickness of the double-sided tape is less than 15um, its adhesion can still reach more than 1kg / in. The double-sided tape made can meet the needs of the electronics industry for thinner and higher adhesion.

Description

technical field [0001] The invention relates to the technical field of pressure-sensitive adhesives, in particular to a pressure-sensitive adhesive applied to ultra-thin double-sided adhesives and a preparation method thereof. Background technique [0002] Pressure-sensitive adhesive products are widely used in various industries such as packaging, electrical appliances and electronics, construction, medical and health care, automobiles and household daily necessities, and play various bonding functions such as bundling, protection, sealing, insulation and fixing. In recent years, electronic products have generally used structural adhesives or double-sided adhesives instead of traditional screws as assembly components. Therefore, in response to the thinner design of electronic products, there is also a requirement for the total thickness of double-sided adhesives to be thinner. However, most of the PET double-sided adhesives currently on the market are made of traditional ac...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J133/08C09J145/00C09J7/02C09J11/06C08F220/18C08F220/28C08F218/08
Inventor 游群芳
Owner 东莞宏石功能材料科技有限公司