Method for making pottery brick material by modifying gold ore tailings with weakly acidic clay

A technology of gold mine tailings and weak acidity, applied in the field of tailings resource utilization technology and materials, to reduce production costs and waste

Active Publication Date: 2015-10-21
NORTHEASTERN UNIV LIAONING
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Tailings are also a special mineral resource, but its resource utilization, reduction and efficient utilization are still a challenge

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for making pottery brick material by modifying gold ore tailings with weakly acidic clay
  • Method for making pottery brick material by modifying gold ore tailings with weakly acidic clay
  • Method for making pottery brick material by modifying gold ore tailings with weakly acidic clay

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0059] First put an appropriate amount of water into the mixer, start the mixer, then add red weak acid clay, the mass ratio of weak acid clay to water is 25:4, and stir at a constant speed with the mixer to form a solid-liquid mixture of weak acid clay and water System, that is, the modified initial solution; let the modified initial solution stand at room temperature for 3-5 hours to obtain a weakly acidic modified initial solution with pH=6~7; put the weakly acidic modified initial solution into the mixer, and start the mixer , slowly add skarn-type gold tailings into the weakly acidic modified initial solution at a uniform rate, the mass ratio of gold tailings to weakly acidic clay is 1:1, stir at a constant speed with a mixer, and use weakly acidic modified initial solution to The gold tailings are modified to obtain a mixed system of "modified tailings-modified initial liquid"; the stirring process of the mixer runs through the whole process. Put the "modified tailings-m...

Embodiment 2

[0062] First put an appropriate amount of water into the mixer, start the mixer, then add red weak acid clay, the mass ratio of weak acid clay to water is 5:2, stir at a constant speed with the mixer to form a solid-liquid mixture of weak acid clay and water System, that is, the modified initial solution; let the modified initial solution stand at room temperature for 3-5 hours to obtain a weakly acidic modified initial solution with pH=6~7; put the weakly acidic modified initial solution into the mixer, and start the mixer , slowly add skarn-type gold tailings into the weakly acidic modified initial solution at a uniform rate. The gold tailings are modified to obtain a mixed system of "modified tailings-modified initial liquid"; the stirring process of the mixer runs through the whole process. Put the "modified tailings-modified initial liquid" mixed system for standing maintenance at room temperature, and when the system has a certain plasticity, the curing is completed, and...

Embodiment 3

[0065] First put an appropriate amount of water into the mixer, start the mixer, then add cyan weak acid clay, the mass ratio of weak acid clay to water is 2:1, stir at a constant speed with the mixer to form a solid-liquid mixture of weak acid clay and water System, that is, the modified initial solution; let the modified initial solution stand at room temperature for 3-5 hours to obtain a weakly acidic modified initial solution with pH=6~7; put the weakly acidic modified initial solution into the mixer, and start the mixer , slowly add ductile shear band type gold tailings into the weakly acidic modified initial solution at a uniform rate, the mass ratio of gold tailings to weakly acidic clay is 4:1, stir at a constant speed with a mixer, and use weakly acidic modified initial solution The gold tailings are modified to obtain a "modified tailings-modified initial liquid" mixed system; the stirring process of the mixer runs through the whole process. Put the "modified tailing...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
modulusaaaaaaaaaa
water absorptionaaaaaaaaaa
water absorptionaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for making a ceramic tile material by modifying gold ore tailings by utilizing weakly acidic clays, and belongs to the technical fields of tailing recycling and materials. The method comprises the following steps: standing the weakly acidic clays and a water solid-liquid mixing system at normal temperature for certain time to form an initial solution of modified tailings; then allocating the gold ore tailings into an initial solution system for modification; maintaining a mixed system formed by obtained modified gold tailings and the modified initial solution, and carrying out sufficient reaction on the weakly acidic modified initial solution and the modified gold tailings to form a blank body for preparing a ceramic tile; finally preparing the ceramic tile material by virtue of extrusion and electrical kiln burning. The ceramic tile material can not only be used as an unglazed ceramic tile material, but also be used as a glazed ceramic tile material after the surface is glazed. The invention provides a new technical method for realizing the high-efficiency decrement utilization of the gold tailings and seeking a low-cost novel resource for the ceramic tile material.

Description

technical field [0001] The invention relates to a method for making pottery bricks by using weakly acidic clay modified gold ore tailings, and belongs to the technical field of tailings resource utilization technology and materials. Background technique [0002] The relative content of gold minerals in gold deposits is very small, so that the amount of tailings produced during the mining process is particularly large, which causes great harm to the ecological environment and people's lives. Tailings are also a special mineral resource, but its resource utilization, reduction and efficient utilization are still a challenge. [0003] Clay is an inexpensive material that is widely distributed. Ceramic brick materials are widely used in daily life, urban construction, etc., and the amount of raw materials used and the amount of waste in the production process are large. If the ceramic brick material is produced by the method provided by the invention, on the one hand, the prod...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B33/132C04B33/22
CPCY02P40/60
Inventor 黄菲刘睿
Owner NORTHEASTERN UNIV LIAONING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com