Al-Based Bulk Metallic Glass Alloys with Large Subcooled Liquid Interval Containing Er

A technology of supercooled liquid phase and metallic glass, which is applied in the field of new materials to achieve the effects of good mechanical properties, low glass transition temperature, and large glass forming ability

Active Publication Date: 2016-08-24
DALIAN UNIV OF TECH
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The present invention aims at the deficiency in the development of Al-based metallic glass at present, and provides an Al-based bulk metallic glass alloy containing Er

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Al-Based Bulk Metallic Glass Alloys with Large Subcooled Liquid Interval Containing Er
  • Al-Based Bulk Metallic Glass Alloys with Large Subcooled Liquid Interval Containing Er
  • Al-Based Bulk Metallic Glass Alloys with Large Subcooled Liquid Interval Containing Er

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Al 85 Ni 6.8 co 2.2 Er 4 La 2 Preparation, structure and performance testing of bulk metallic glass alloys:

[0019] Step 1: Al, Ni, Co, Er and La raw materials with a purity greater than 95wt.% are used for compounding according to the composition expression.

[0020] Step 2: Preparation of master alloy ingot: Put the raw materials with a good ratio into the copper crucible of the non-consumable electric arc furnace, and evacuate to 2×10 -3 Pa, filled with argon gas, then arc smelted and the alloy was smelted repeatedly 4 times to obtain a master alloy ingot with uniform composition.

[0021] Step 3: Preparation of metallic glass powder: Put the master alloy ingot into the powder making equipment and vacuumize to 2×10 -3 Pa, fill with argon gas, and heat the master alloy to a molten state by high-frequency induction melting. Turn on the spray switch, let the molten metal liquid pass through the high-pressure argon gas, use the high-pressure gas to spray the allo...

Embodiment 2

[0029] Al 85 Ni 6.8 co 2.2 Er 3 La 3 Preparation, structure and performance testing of bulk metallic glass alloys:

[0030] (1) Al, Ni, Co, Er and La raw materials with a purity greater than 95wt.% are used for batching according to the composition expression;

[0031] (2) The implementation steps of master alloy ingot preparation, metallic glass powder and rod preparation, and alloy performance testing are the same as in Example 1, and the detailed data are listed in the attached table.

Embodiment 3

[0033] Al 86 Ni 6 co 2 Er 4 La 2 Preparation, structure and performance testing of bulk metallic glass alloys:

[0034] (1) Al, Ni, Co, Er and La raw materials with a purity greater than 95wt.% are used for batching according to the composition expression;

[0035] (2) The implementation steps of master alloy ingot preparation, metallic glass powder and rod preparation, and alloy performance testing are the same as in Example 1, and the detailed data are listed in the attached table.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
critical dimensionaaaaaaaaaa
critical dimensionaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to an Al-based bulk metallic glass alloy containing Er in a large supercooled liquid phase interval, belonging to the technical field of new materials. The specific composition expression is Al a Ni b co c Fe d Ag e Er f La g , where a, b, c, d, e, f and g represent the atomic percentages of the corresponding elements, where 2≤b≤9, 0≤c≤3, 0≤d≤6, 0≤e≤3, 2≤f≤7, 0≤g≤4, and a+b+c+d+e+f+g=100, 6≤b+c+d≤10 and 5≤f+g≤9. The alloy has a large glass-forming ability, and a bulk metallic glass alloy rod with a critical diameter of 1.2mm can be prepared by copper mold casting; the alloy also has a supercooled liquid phase range of 26-40°C and good mechanical properties. Performance, the breaking strength is 1.11-1.24GPa, the specific strength is 319-348kN·m / kg, the plastic strain is 0.1%-0.4%, and the Vickers hardness is 362-385.

Description

Technical field: [0001] The invention belongs to the technical field of new materials, and relates to an Er-containing Al-based bulk metallic glass alloy with a large supercooled liquid phase interval. technical background: [0002] Metallic glass (amorphous alloy) refers to a metal alloy in which the atomic arrangement has short-range order and long-range disorder in the solid state. Due to the unique microstructure of metallic glass, it has excellent mechanical properties, physical and chemical properties, such as high strength, high hardness, good corrosion resistance, and viscous flow characteristics in the supercooled liquid phase region. New structural or functional materials. [0003] Among the many metallic glass alloy systems that have been discovered, Al-based metallic glass exhibits the characteristics of high specific strength, high toughness and good corrosion resistance. potential application. At present, people have multiple alloy systems (such as: Al-Ni-Co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C45/08
Inventor 张伟朱正旺李艳辉
Owner DALIAN UNIV OF TECH