A kind of manufacturing process of ceramic LED lamp

A technology of LED lamp and manufacturing process, which is applied in the field of ceramic LED lamps, can solve the problems of poor energy saving effect and waste of electric energy, and achieve the effect of high quality and yield, thin flowers and leaves, and clearly visible veins

Inactive Publication Date: 2016-03-30
洛阳牡丹瓷研究院
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, its existing problems are: ordinary lamps are generally used, and in today's increasingly tense fossil energy, the waste of electric energy is relatively large, and the energy-saving effect is poor.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A manufacturing process of a ceramic LED lamp, comprising the following steps:

[0021] (1) Take the prepared ceramic clay raw material, put the raw material, ball stones and water into the ball mill according to the weight ratio of 1:1:1 and mix it for 8 hours, then take it out, pour it into a plastic bucket, and pass it through a 300-mesh sieve. Precipitate for 8 hours, pour out the upper layer of clear water, put the sediment into a vacuum mud filter and filter it into mud, and make ceramic mud for later use;

[0022] The raw material of described ceramic mud is made up of the material of following parts by weight, SiO 2 60 copies, AL 2 o 3 20 parts, Fe 2 o 3 0.3 part, CaO0.01 part, MgO0.01 part, K 2 O2.5 parts, Na 2 O0.15 parts, TiO 2 0.04 parts.

[0023] (2) Take the porcelain clay prepared in step (1) and make petals of various shapes, large, medium and small, for use. The thickness of the petals is required to be uniform and not more than 1mm, and the pet...

Embodiment 2

[0030] A manufacturing process of a ceramic LED lamp, comprising the following steps:

[0031] (1) Take the prepared ceramic clay raw material, put the raw material, ball stone and water into the ball mill according to the weight ratio of 1:1:1 and mix it for 8-12 hours, then take it out, pour it into a plastic bucket, and pass through 300 mesh Sieve, settle for 8-10 hours, pour out the upper layer of clear water, put the sediment into a vacuum mud filter and filter it into mud, and make ceramic mud for later use;

[0032] The raw material of described ceramic mud is made up of the material of following parts by weight, SiO 2 70 copies, AL 2 o 3 30 parts, Fe 2 o 3 ~0.4 parts, CaO0.01 parts, MgO0.01 parts, K 2 0~2.8 parts, Na 2 0~0.17 parts, TiO 2 0.04 parts.

[0033] (2) Take the porcelain clay prepared in step (1) and make petals of various shapes, large, medium and small, for use. The thickness of the petals is required to be uniform and not more than 1mm, and the peta...

Embodiment 3

[0043] A manufacturing process of a ceramic LED lamp, comprising the following steps:

[0044] (1) Take the prepared ceramic clay raw material, put the raw material, ball stone and water into the ball mill according to the weight ratio of 1:1:1 and mix it for 8-12 hours, then take it out, pour it into a plastic bucket, and pass through 300 mesh Sieve, settle for 8-10 hours, pour out the upper layer of clear water, put the sediment into a vacuum mud filter and filter it into mud, and make ceramic mud for later use;

[0045] The raw material of described ceramic mud is made up of the material of following parts by weight, SiO 2 65 copies, AL 2 o 3 25 parts, Fe 2 o 3 0.35 parts, CaO0.01 parts, MgO0.01 parts, K 2 O2.56 parts, Na 2 O0.16 parts, TiO 2 0.04 parts.

[0046] (2) Take the porcelain clay prepared in step (1) and make petals of various shapes, large, medium and small, for use. The thickness of the petals is required to be uniform and not more than 1mm, and the pet...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a manufacturing process of a ceramic LED lamp, comprising the following steps: (1) taking porcelain clay as a base material to make porcelain clay; (2) making petals of various flower shapes with porcelain clay, glazing and drying; (3) ), take a cylindrical shape tool, and stick the petals around the head end of the cylindrical shape tool layer by layer from small to large, and arrange it into the shape of a flower; (4) glaze; (5), calcined; (6), Take the cylindrical adapter with both ends open, fix the ceramic lamp with the adapter through the cylindrical bottom, and then detachably connect the adapter to the base with the LED lamp to make the finished ceramic LED lamp. The ceramic LED lamp product not only meets the daily lighting needs, but also meets people's aesthetic requirements, and is very suitable for popularization and utilization.

Description

technical field [0001] The invention relates to the technical field of ceramic LED lamps, in particular to a manufacturing process of ceramic LED lamps. Background technique [0002] As we all know, ornamental flowers such as peonies, roses, lotus, chrysanthemums, and peonies have a short flowering period, but the flowers are very bright, which can add a lot of bright spots to indoors or celebrations, but as the saying goes: "Flowers are not always blooming, youth is not always In", it means that although flowers are good, they only bloom for a limited time, and the flowering period is very short; flowers need corresponding ecological conditions to grow and open. It is known that ceramics have existed for thousands of years as a common utensil "including daily necessities such as cups, teapots, and bowls". In my country, pottery was invented as early as about 8000-2000 BC (Neolithic Age). . The main components of ceramic materials are silicon oxide, aluminum oxide, potassiu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/18C04B35/64C04B41/86
Inventor 李学武贾晓莉
Owner 洛阳牡丹瓷研究院