A kind of method of synthesizing superparamagnetic ferric oxide nanosheet

A ferroferric oxide and superparamagnetic technology, applied in the direction of iron oxide/iron hydroxide, nanotechnology, ferrous oxide, etc., can solve the problems of complex process, harsh reaction requirements, large size, etc., and achieve operation Simple, easy to operate, and simple reaction conditions

Inactive Publication Date: 2016-05-18
TONGJI UNIV
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The products obtained by these methods have large size, poor dispersibility and harsh reaction requirements, and the process is more complicated

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of method of synthesizing superparamagnetic ferric oxide nanosheet
  • A kind of method of synthesizing superparamagnetic ferric oxide nanosheet
  • A kind of method of synthesizing superparamagnetic ferric oxide nanosheet

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A method for synthesizing superparamagnetic ferric oxide nanosheets, the steps are as follows:

[0020] (1) At room temperature, add trivalent soluble iron salt (ferric chloride) and divalent soluble iron salt (ferrous sulfate) to a certain amount of hydrochloric acid, then add a certain amount of water to prepare a mixed solution of a certain concentration, The mixed solution requires magnetic stirring for several hours to form a uniform mixed solution, wherein the molar ratio of trivalent soluble iron salt to divalent soluble iron salt is 5:1, and the molar ratio of trivalent soluble iron salt to divalent soluble iron salt to hydrochloric acid 4:2:1, and the molar ratio of hydrochloric acid to water is 1:140.

[0021] (2) The mixed solution that step (1) obtains is added dropwise in the 0.5mol / LNaOH solution that contains a certain amount of oleic acid under the vigorous stirring of magnetic stirrer, and the mol ratio of oleic acid and sodium hydroxide is 1: 20, and N...

Embodiment 2

[0026] A method for synthesizing superparamagnetic ferric oxide nanosheets, the steps are as follows:

[0027] (1) At room temperature, add trivalent soluble iron salt (ferric sulfate) and divalent soluble iron salt (ferrous sulfate) to a certain amount of hydrochloric acid, and then add a certain amount of water to prepare a mixed solution with a certain concentration. The mixed solution requires magnetic stirring for several hours to form a uniform mixed solution, wherein the molar ratio of trivalent soluble iron salt to divalent soluble iron salt is 3:2, and the molar ratio of trivalent soluble iron salt, divalent soluble iron salt and hydrochloric acid is 8:4:3, the molar ratio of hydrochloric acid to water is 1:120.

[0028] (2) The mixed solution obtained in step (1) is added dropwise in the 2.0mol / L NaOH solution containing a certain amount of oleic acid under the vigorous stirring of the magnetic stirrer, the mol ratio of oleic acid and sodium hydroxide is 1: 50, NaOH ...

Embodiment 3

[0030] A method for synthesizing superparamagnetic ferric oxide nanosheets, the steps are as follows:

[0031] (1) At room temperature, add trivalent soluble iron salt (ferric thiocyanate) and divalent soluble iron salt (ferrous sulfate) to a certain amount of hydrochloric acid, and then add a certain amount of water to prepare a mixed solution of a certain concentration , the mixed solution requires magnetic stirring for several hours to form a uniform mixed solution, wherein the molar ratio of trivalent soluble iron salt to divalent soluble iron salt is 3:1, and the molar ratio of trivalent soluble iron salt, divalent soluble iron salt and hydrochloric acid The ratio is 8:4:2.5, and the molar ratio of hydrochloric acid to water is 1:130.

[0032] (2) The mixed solution that step (1) obtains is added dropwise in the 1.5mol / LNaOH solution that contains a certain amount of oleic acid under the vigorous stirring of magnetic stirrer, and the mol ratio of oleic acid and sodium hyd...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
sizeaaaaaaaaaa
Login to View More

Abstract

The present invention relates to a method for synthesizing superparamagnetic ferroferric oxide nano-sheets. The method comprises: adding a trivalent soluble iron salt and a divalent soluble iron salt to hydrochloric acid to form a uniform mixed solution, adding the mixed solution to a NaOH solution in a dropwise manner under vigorous stirring, carrying out magnetic attraction on the precipitate after completely reacting, washing a plurality of times with deionized water and ethanol, and carrying out vacuum drying at a temperature of 50-90 DEG C to obtain the superparamagnetic ferroferric oxide nano-sheets. Compared with the method in the prior art, the method of the present invention has characteristics of simple operation, no requirement of inert gas protection, performing at the room temperature, simple reaction conditions and easy operation. The superparamagnetic ferroferric oxide nano-sheets prepared by adopting the reversed-phase co-precipitation method have the small particle, the diameter of 10-30 nm, the saturation magnetization of 77.8 emu / g, and the residual magnetism of 0, and have the superparamagnetism so as to be easily used in the field of biomedicine and bioengineering.

Description

technical field [0001] The invention belongs to the technical field of inorganic nanometer materials, and in particular relates to a method for synthesizing superparamagnetic ferric iron tetroxide nanosheets under a non-inert atmosphere. Background technique [0002] Nano Fe 3 o 4 It has compatibility with biological tissue and electrical and magnetic properties related to size and shape, making it widely used in magnetic ink, electronic and biological sensitive materials, magnetic fluid and magnetic recording materials, high-density magnetic recording media and biomedicine, etc. field has a wide range of applications. Therefore, it has become one of the hotspots of the majority of scientific research workers. Since superparamagnetic ferric oxide nanomaterials have broader application prospects in the fields of biomedicine, immunity, and environmental science, the preparation of superparamagnetic nanomaterials has also become one of the focuses of everyone's research. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01G49/08B82Y40/00
Inventor 陈云吴庆生夏一鸣李静
Owner TONGJI UNIV