Formula and production process for producing high-quality porcelain by using poor-quality raw materials

A production process and high-quality technology, applied in the field of ceramic manufacturing, can solve the problems of increasing production cost, restricting the development of Dehua ceramic enterprises, and restricting production scale, so as to achieve the effect of reducing production cost, shortening the supply time of raw materials, and improving economic benefits

Active Publication Date: 2015-03-04
福建省德化县宏达陶瓷有限公司
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In recent years, with the continuous expansion of Dehua's export of ceramics, the demand for ceramic raw materials has also increased. Dehua does not produce high-quality ceramic raw materials locally, and the price of domestic high-quality ceramic raw materials continues to rise, resulting in production costs. The increase and production scale are restricted, and the dependence on high-quality raw materials supplied from outside has become a bottleneck restricting the development of Dehua ceramic enterprises.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0032] The blank formula is as follows in parts by weight: the blank formula of porcelain is as follows in parts by weight: 27 parts of weathered feldspar, 16 parts of No. 1 china clay, 20 parts of No. 2 china clay, 15 parts of No. 3 china clay, 11 parts of No. 4 china clay, black clay 4 parts, 6 parts of kaolin, 1 part of black talc;

[0033] No. 1 porcelain clay is as follows according to mass percentage: SiO 2 66.2、Al 2 o 3 16.1 Fe 2 o 3 1.3, CaO 0.2, MgO 0.08, K 2 O 1.9, Na 2 O 1.1, TiO 2 0.4, IL 12.72;

[0034] No. 2 porcelain clay is as follows according to mass percentage: SiO 2 64.8, Al 2 o 3 12.8 Fe 2 o 3 1.28, CaO 0.1, MgO 0.1, K 2 O 1.6, Na 2 O 1.3, TiO 2 0.2, IL 17.91;

[0035] No. 3 porcelain clay is as follows according to mass percentage: SiO 2 47. Al 2 o 3 35. Fe 2 o 3 1.0, CaO 0.05, MgO 0.5, K 2 O 0.8, Na 2 O 0.5, TiO 2 0.5, IL 14.65;

[0036] No. 4 porcelain clay is as follows according to mass percentage: SiO 2 63.4、Al ...

specific Embodiment 2

[0037] The blank formula is as follows in parts by weight: 23 parts of weathered feldspar, 8 parts of No. 1 china clay, 24 parts of No. 2 china clay, 16 parts of No. 3 china clay, 14 parts of No. 4 china clay, 4 parts of black clay, 8 parts of kaolin, 3 parts of black talc share;

[0038] No. 1 china clay, No. 2 china clay, No. 3 china clay and No. 4 china clay select the same raw materials as the specific examples.

[0039] A manufacturing process for making high-quality porcelain by using inferior raw materials, characterized in that, adopting the blank formula described in any one of the above items, comprising the following steps:

[0040] Step 1: According to the billet formula, weigh and proportion, mix the billet with wet ball mill, and make mud, wherein the ratio of mud, ball, and water is 1:2:1.5, and the mud fineness is less than 1%, and pass through a 320-mesh sieve and wait for use;

[0041] Step 2, the mud is press-filtered into mud cake, stale mud, and rolled i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
shrinkageaaaaaaaaaa
water absorptionaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the field of ceramic production, and particularly relates to a formula and a production process for producing a high-quality porcelain by using poor quality raw materials such as weathered feldspar, porcelain sand, red soil and other poor-quality raw materials. According to the formula, the weathered feldspar, the black clay, the kaolin, the black talc and the porcelain clay produced in the Dehua are subjected to the production process with characteristics of reasonable formula and right control so as to produce the daily-use porcelain meeting the export standard, such that the bottleneck problem constraining the Dehua exported ceramic enterprise development is solved, the production cost is substantially reduced, the raw material supply time is shortened, the economic efficiency is improved, the market competitiveness of the exported ceramic enterprise is enhanced, and the great promotional value and the great social and economic benefits are provided.

Description

technical field [0001] The invention belongs to the field of ceramic manufacturing, and in particular relates to a formula and a manufacturing process for high-quality porcelain made of inferior raw materials such as weathered feldspar, porcelain sand, and laterite. Background technique [0002] Dehua has a long history of ceramic production, and is the birthplace of my country's ceramic culture and one of the three major ancient porcelain capitals. More than 80% of Dehua ceramic products are exported to more than 190 countries and regions. It is one of the top ten key export counties (cities) in Fujian Province. One, the country's largest production and export base of craft ceramics. [0003] In recent years, with the continuous expansion of the scale of Dehua's export of ceramics, the demand for ceramic raw materials has also increased. Dehua does not produce high-quality ceramic raw materials locally, and the price of domestic high-quality ceramic raw materials continues t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/13C04B33/34
Inventor 曾成志
Owner 福建省德化县宏达陶瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap